Silica nano-particle/polyelectrolyte nanocomopsite membranes for direct methanol fuel cells

Ying-Ling Liu,Yu-Huei Su,Juin-Yih Lai

2006-01-01

Abstract:Modification on PEMs to improve their thermal and chemical stability and to depress their methanol crossover is another approach to provide high performance PEMs. Organic-inorganic nanocomposites represent a useful approach to PEM modification. Layered clays and silica nanoparticles are two major inorganic reinforcements in PEM modifications. Clay incorporation into PEMs introduces a winding pathway for a methanol molecule to reduce their methanol crossover. The presence of silica nanoparticles in PEMs keep their hydrophilicity to maintaining water and improve their thermal and mechanical stability. The methanol crossover of PEMs is also depressed with formation of polyelectrolyte-silica nanocomposites as reduction of their swelling degree in methanol fuel solutions. Incorporation of nanosized inorganic reinforcements to proton exchange membranes, although brough about membrane stabilization, however would certainly lower their ion exchange capacity and proton conductivity. To overcome this problem, Lee et al prepared sulfonated montmorillonite to modify Nafion. The prepared composite membranes showed dramatic decreases in methanol permeability and comparable proton conductivity to pristine Nafion membranes. Bébin et al also used sulfonated Laponite particles to prepare Nafion/clay-SO3H composite membranes. The performance of the membrane-electrolyte assembly using the composite membrane is better than the one of a Nafion membrane. The above articles suggested that uses of sulfonated inorganic particles in preparation of polyelectrolytes nanocomposite membranes is an effective approach to improve the proton exchange membrane performances. Instead of clay, in this work silica nanoparticles and their sulfonated forms (silica-SO3H) were utilized in preparation of polyelectrolyte/silica nanocomposite membranes. Sulfonated poly(phthalazinone ether ketone) (sPPEK) with a high content of sulfonic acid groups is utilized as the proton conducting material. The properties of the prepared nanocomposite PEMs are examined and discussed. The chemical structures of sPPEK polyelectrolyte and silica-SO3H nanoparticles are shown in Figure 1. Mixing of these two substances in DMAc formed homogeneous and transparent solutions. sPPEK/silica-SO3H nanocomposite membranes possessing various silica-SO3H contents (NM-SA-X, X = silica-SO3H (g)/100g of sPPEK in solutions) were prepared from solution casting on glass plates. All obtained membranes showed high transparency, indicating the silica particles did not aggregate during membrane preparation.