Abstract:Polycrystalline Ni of two purities (99.967% (4N) and 99.5% (2N)) was deformed to an ultra-high strain of εvM=100 (εvM, von Mises strain) by high pressure torsion at room temperature. The 4N and 2N samples at this strain are nanostructured with an average boundary spacing of ∼100nm, a high density of dislocations and a large fraction of high angle boundaries (>15°) of 0.68–0.74, as determined by transmission electron microscopy, and 0.8–0.83, as determined by electron backscattering diffraction. The deformed samples were annealed isochronally for 1h at temperatures from 100 to 600°C, and the evolution of the structural parameters (boundary spacing, average boundary misorientation angle and the fraction of high angle boundaries), crystallographic texture and hardness were determined. Based on microstructural parameters the energy stored in the deformed state was estimated to be 14MPa and 24MPa for 4N Ni and 2N Ni, respectively. The isochronal annealing leads to a drop in hardness in three stages: a relatively small decrease at low temperatures (recovery), followed by a rapid decrease at intermediate temperatures (recrystallization) and a slow decrease at high temperature (grain growth). Both recovery and recrystallization of the 2N Ni are strongly retarded by the presence of impurities reducing the mobility of boundaries. In the recrystallization stage, changes in hardness, microstructure and texture show that the 4N Ni recrystallizes discontinuously, in spite of a large fraction of high angle boundaries in the deformed state. This finding contradicts previous experiments and theory, which suggest that recrystallization is continuous when the fraction of high angle boundaries is high. In the 2N Ni, the observations suggest that some structural coarsening (continuous recrystallization) may take place simultaneously with discontinuous recrystallization. The findings emphasize the importance of alloying, which can delay the process of recovery and recrystallization and thereby enable tailoring of the microstructure and properties through an optimized annealing treatment.

A methodology for determining mechanical properties of nanomaterials at high pressure and temperature

Thermomechanics of nanocrystalline nickel under high pressure-temperature conditions.

High P–T Nano-Mechanics of Polycrystalline Nickel

HighP-TNano-Mechanics of Polycrystalline Nickel.

Microstrain and grain-size analysis from diffraction peak width and graphical derivation of high-pressure thermomechanics

A Molecular Dynamics Study on Mechanical Performance and Deformation Mechanisms in Nanotwinned NiCo-based Alloys with Nano-Precipitates under High Temperatures

Energy dissipation of materials at high pressure and high temperature.

First-principles Study of Mechanical Properties and Electronic Structures of the Nickel-molybdenum Binary Compounds Under Pressure

Dynamic Compressive Behavior of a Single Crystal Nickel-Base Superalloy at Ultra-High Temperature: Mechanism Investigation with a Modified Electric Synchronous SHPB Technique

Recent Findings on the Mechanical Responses of Nanostructures to Extreme Loading Conditions

Compressive-tensile Deformation of Nanocrystalline Nickel at High Pressure and Temperature Conditions

Nanoindentation Study and Mechanical Property Analysis of Nickel-Based Single Crystal Superalloys

Dynamic tensile properties of a single crystal Nickel-base superalloy at high temperatures measured with an improved SHTB technique

Synchrotron X-ray powder diffraction under high pressures up to 33 MPa for mechanoresponsive materials

Thermal Behavior of Ni (99.967% and 99.5% Purity) Deformed to an Ultra-High Strain by High Pressure Torsion

Microstructures of Nickel Deformed by High Pressure Torsion to High Strains

Structural Evolution and Mechanical Behaviour of Pt Nanoparticle Superlattices at High Pressure.

Thermal behavior of pure Ni deformed by high pressure torsion to ultra-high strain

Grain size effects on the compressibility and yield strength of copper

Comparative Studies of Compressibility Between Nanocrystalline and Bulk Nickel

Compressibility of Nickel Nanoparticle Chain