Abstract:Polycrystalline Ni of two purities (99.967% (4N) and 99.5% (2N)) was deformed to an ultra-high strain of εvM=100 (εvM, von Mises strain) by high pressure torsion at room temperature. The 4N and 2N samples at this strain are nanostructured with an average boundary spacing of ∼100nm, a high density of dislocations and a large fraction of high angle boundaries (>15°) of 0.68–0.74, as determined by transmission electron microscopy, and 0.8–0.83, as determined by electron backscattering diffraction. The deformed samples were annealed isochronally for 1h at temperatures from 100 to 600°C, and the evolution of the structural parameters (boundary spacing, average boundary misorientation angle and the fraction of high angle boundaries), crystallographic texture and hardness were determined. Based on microstructural parameters the energy stored in the deformed state was estimated to be 14MPa and 24MPa for 4N Ni and 2N Ni, respectively. The isochronal annealing leads to a drop in hardness in three stages: a relatively small decrease at low temperatures (recovery), followed by a rapid decrease at intermediate temperatures (recrystallization) and a slow decrease at high temperature (grain growth). Both recovery and recrystallization of the 2N Ni are strongly retarded by the presence of impurities reducing the mobility of boundaries. In the recrystallization stage, changes in hardness, microstructure and texture show that the 4N Ni recrystallizes discontinuously, in spite of a large fraction of high angle boundaries in the deformed state. This finding contradicts previous experiments and theory, which suggest that recrystallization is continuous when the fraction of high angle boundaries is high. In the 2N Ni, the observations suggest that some structural coarsening (continuous recrystallization) may take place simultaneously with discontinuous recrystallization. The findings emphasize the importance of alloying, which can delay the process of recovery and recrystallization and thereby enable tailoring of the microstructure and properties through an optimized annealing treatment.

Thermomechanics of nanocrystalline nickel under high pressure-temperature conditions.

High P–T Nano-Mechanics of Polycrystalline Nickel

HighP-TNano-Mechanics of Polycrystalline Nickel.

A methodology for determining mechanical properties of nanomaterials at high pressure and temperature

A Molecular Dynamics Study on Mechanical Performance and Deformation Mechanisms in Nanotwinned NiCo-based Alloys with Nano-Precipitates under High Temperatures

Microstructures of Nickel Deformed by High Pressure Torsion to High Strains

Compressive-tensile Deformation of Nanocrystalline Nickel at High Pressure and Temperature Conditions

Thermal Behavior of Ni (99.967% and 99.5% Purity) Deformed to an Ultra-High Strain by High Pressure Torsion

Thermal behavior of pure Ni deformed by high pressure torsion to ultra-high strain

Microstrain and grain-size analysis from diffraction peak width and graphical derivation of high-pressure thermomechanics

Nanoindentation Study and Mechanical Property Analysis of Nickel-Based Single Crystal Superalloys

First-principles Study of Ni-Al Intermetallic Compounds under Various Temperature and Pressure

Superplasticity and Microstructure Evolution of Electrodeposited Nanocrystalline Nickel

First-principles Study of Mechanical Properties and Electronic Structures of the Nickel-molybdenum Binary Compounds Under Pressure

Compression Behavior of Nanocrystalline Nickel at 77 K

Dynamic Compressive Behavior of a Single Crystal Nickel-Base Superalloy at Ultra-High Temperature: Mechanism Investigation with a Modified Electric Synchronous SHPB Technique

Compressive Behavior of Nanocrystalline Nickel at Various Temperatures and Strain Rates

Effect of Temperature on Deformation and Fracture Behaviour of Nanostructured Polycrystalline Ni under Tensile Hydrostatic Stress by Molecular Dynamics Simulation

Comparative Studies of Compressibility Between Nanocrystalline and Bulk Nickel

High Strain Rate Compressive Deformation Behavior of Nickel Microparticles

Texture of Nanocrystalline Nickel: Probing the Lower Size Limit of Dislocation Activity