Structural, Optical, and Magnetic Properties of o‐TbFeO3 Nanomaterials Synthesized by the co‐Precipitation Method
Nguyen Anh Tien,Huynh Thi Kim Hoang,Valentina Olegovna Mittova,Tran Thi To Nga,Nguyen Thi Truc Linh,Irina Yakovlevna Mittova,Elena Viktorovna Tomina,Tran Dinh Trinh,Le Thi Thanh Thuy,Thanh Son Cam
DOI: https://doi.org/10.1002/slct.202303386
2023-12-15
ChemistrySelect
Abstract:Text for Table of Contents. Using iron and terbium nitrates as precursors, the perovskite‐like TbFeO3 was obtained. The calcination temperature for producing a homogeneous phase of TbFeO3 was 850 °C. The product was a paramagnetic nanomaterial with a low coercivity value and a high net magnetization value. The material absorbed visible light with a direct bandgap of about 2.68 eV. Following the co‐precipitation method for producing terbium orthoferrite (TbFeO3), the final products were denoted as TbFeO3‐650, −750, and −850. A single‐phase of orthorhombic TbFeO3 crystals (o‐TbFeO3) was obtained with a calcination temperature of up to 850 °C, while in the range of 650–750 °C there was still a small amount of terbium and iron oxide phases. The average size of o‐TbFeO3 crystallites for the TbFeO3‐850 sample was about 76 nm and was larger than that of TbFeO3‐650 (~45 nm) and TbFeO3‐750 (~47 nm). The o‐TbFeO3 crystal structure in all samples was found to be distorted. In the applied field from −15 to +15 kOe, all of the samples had low values of coercive field (5–11 ⋅ 10−3 Oe) but high values of net magnetization (2.06–2.40 emu ⋅ g−1); the samples appeared to behave as paramagnetic materials. It was shown that the TbFeO3‐850 sample has slightly better magnetic properties than the two others. An average grain size of about 79 nm was found in the TbFeO3‐850 sample, which exhibited a morphology of sphere‐like shapes with highly agglomerated grains. The TbFeO3‐850 sample demonstrated a high absorbance at wavelengths of 400–600 nm, with a direct bandgap of about 2.68 eV.
chemistry, multidisciplinary