Enhancing the Performance of Symmetrical Solid Oxide Fuel Cells with Sr2Fe1.5Mo0.5O6-δ Electrodes Via Infiltration of Pr6O11 Bifunctional Catalyst

Zongchao Zhu,Keqiang Sun,Dong Xu,Yiheng Gu,Qing Ni,Yifeng Zheng,Han Chen,Lin Ge,Xiaogu Huang,Lucun Guo

DOI: https://doi.org/10.1016/j.electacta.2021.139569

IF: 6.6

2022-01-01

Electrochimica Acta

Abstract:Symmetrical solid oxide fuel cells based on yttrium-stabilized zirconia (YSZ) electrolyte and Sr2Fe1.5Mo0.5O6-delta (SFM) electrode are prepared via phase-inversion and impregnation processes. The YSZ symmetrical electrolyte support is constructed using two porous frameworks and one thin-dense-membrane via phase-inversion combined with drip-coating techniques. SFM is infiltrated into the porous frameworks of the symmetric YSZ support to work as electrodes. Nanoscale Pr6O11 catalysts are further infiltrated into the electrodes to promote electrochemical performance. The optimal loading of SFM and Pr6O11 are systematically investigated. At 800 degrees C, with the optimal loading of SFM (12 wt%), the polarization resistance (R-p) for anode and cathode of the cell decrease to 0.19 and 0.10 Omega.cm(2), respectively. The maximum power density (MPD) achieves 301 mW.cm(-2) in H-2 at 800 degrees C. After loading Pr6O11, the R-p for anode and cathode further decrease by 47% to 0.10 Omega.cm(2) and by 80% to 0.021 Omega.cm(2), respectively. And the MPD improves by 51% to 455 mW.cm(-2) (at 800 degrees C). These results and analysis of distribution of relaxation times demonstrate that the introduction of Pr6O11 as bifunctional catalysts is a promising approach for simultaneously improving H-2 fuel oxidation and O-2 reduction activities. (C) 2021 Elsevier Ltd. All rights reserved.