Abstract:This study was to investigate direct electrolysis of CO2 via solid oxide cells with thin Y0.16Zr0.84O1.92 (YSZ) electrolytes and (La0.8Sr0.2)(0.)95MnO3-delta (LSM)-YSZ air electrodes supported on La0.8Sr0.2Cr0.5Fe0.5O3-delta (LSCrF)YSZ fuel electrodes. The fuel electrode with straight open pores was prepared using the phase-inversion tape casting method, modified with nano-scaled Sr(2)FeLsMn(0)(.5)O(6-delta) (SFM) catalysts using the impregnation method. Substantially larger maximum power densities were observed in the fuel cell mode for single cells with the SFM catalysts than without, e.g., 423 vs. 51 mW.cm(-2) at 800 degrees C. Impedance analysis showed an order magnitude drop in the pure ohmic resistances and the interfacial polarization resistances in the presence of electronically conductive and catalytically active SFM nanoparticulates. Electrolysis measurements indicated that these nanoscaled SFM catalysts also helped to promote CO2 reduction reactions. The electrolysis current densities at 1.5 V were 0.48, 0.64 and 1.02 A.cm(-2) for the SFM-infiltrated cells at 700, 750, 800 degrees C, respectively. In contrast, the blank cells displayed much smaller current densities of 0.22, 0.35 and 0.41 A.cm(-2) under the similar conditions. Apparently, the modification of the LSCrF-YSZ electrode with SFM nanoparticulates provided extended electrochemically active sites with sufficient interconnected paths to transfer electrons and oxygen ions, which led to a significant increase in the electrochemical performance. The reduced polarization resistance and high current density show that the nano-scaled SFM-modified LSCrF-YSZ fuel electrode is highly effective for pure CO2 electrolysis without using the safe gas.

Symmetrical Solid Oxide Fuel Cells Fabricated by Phase Inversion Tape Casting with Impregnated SrFe0.75Mo0.25O3-δ (SFMO) Electrodes

Symmetrical Solid Oxide Fuel Cells with Impregnated SrFe0.75Mo0.25O3−δ Electrodes

Infiltrated Sr 2 Fe 1.5 Mo 0.5 O 6 /la 0.9 Sr 0.1 Ga 0.8 Mg 0.2 O 3 Electrodes Towards High Performance Symmetrical Solid Oxide Fuel Cells Fabricated by an Ultra-Fast and Time-Saving Procedure

Characterization of Symmetrical SrFe0.75Mo0.25O3−δ Electrodes in Direct Carbon Solid Oxide Fuel Cells

Synthesis and Evaluation of Ca-doped Sr2Fe1.5Mo0.5O6-δ As Symmetrical Electrodes for High Performance Solid Oxide Fuel Cells

Enhancing the Performance of Symmetrical Solid Oxide Fuel Cells with Sr2Fe1.5Mo0.5O6-δ Electrodes Via Infiltration of Pr6O11 Bifunctional Catalyst

Novel Metal-Supported Solid Oxide Fuel Cells With Impregnated Symmetric La0.6sr0.4fe0.9sc0.1o3-Delta Electrodes

Electrochemical Performance and Anode Reaction Process for Ca Doped Sr2Fe1·5Mo0·5O6-δ As Electrodes for Symmetrical Solid Oxide Fuel Cells

Tuning Layer-Structured La0.6sr1.4mno4+Delta Into A Promising Electrode For Intermediate-Temperature Symmetrical Solid Oxide Fuel Cells Through Surface Modification

SrFe0.75Mo0.25O3− Impregnated 430L Alloys for Efficient Fuel Oxidation in Metal Supported Solid Oxide Fuel Cells

Ni Doped La0.6Sr0.4FeO3-δ Symmetrical Electrode for Solid Oxide Fuel Cells

A Redox−reversible Perovskite Electrode for CeO2− and LaGaO3−based Symmetric Solid Oxide Fuel Cells

Fabrication and Optimization of La 0.4 Sr 0.6 Co 0.2 Fe 0.7 Nb 0.1 O 3- Δ Electrode for Symmetric Solid Oxide Fuel Cell with Zirconia Based Electrolyte

Metal-supported solid oxide fuel cells with impregnated SrFe 0.75Mo0.25O3 cathodes

Sr2Fe1.5Mo0.5O6−δ- Sm0.2Ce0.8O1.9Composite Anodes for Intermediate-Temperature Solid Oxide Fuel Cells

Sr2Fe1.5Mo0.5O6 As Cathodes for Intermediate-Temperature Solid Oxide Fuel Cells with La0.8Sr0.2Ga0.87Mg0.13O3 Electrolyte

Improved Performance of a Symmetrical Solid Oxide Fuel Cell by Swapping the Roles of Doped Ceria and La0.6Sr1.4MnO4+δ in the Electrode

Co-synthesis of LSCFN-GDC Electrode for Symmetric Solid Oxide Fuel Cell Running on Propane

Sc-substituted La0.6Sr0.4FeO3−δ Mixed Conducting Oxides As Promising Electrodes for Symmetrical Solid Oxide Fuel Cells

Direct Electrolysis of CO2 in Solid Oxide Cells Supported on Ceramic Fuel Electrodes with Straight Open Pores and Coated Catalysts

High-performance SOFCs with Impregnated Sr2Fe1.5Mo0.5O6-δ Anodes Toward Sulfur Resistance