Abstract:TC4 titanium alloy wire arc additive manufacturing (WAAM) is easy to produce coarse columnar β grain structure which affects mechanical properties. So in this paper, an innovative process of interpass milling assisted TC4 titanium alloy gas tungsten arc welding (GTAW) WAAM is proposed. The controlling interpass milling depth is used to improve the microstructure and mechanical properties of TC4 titanium alloy parts during the GTAW-WAAM. The results showed that the coarse columnar β grains and fine α phase were observed in the non-interpass milling part. When the interpass milling assistance GTAW-WAAM was employed, the coarse columnar β grains transformed into short columnar and equiaxed grains. With the increased of interpass milling depth, the average size of α phase was gradually refined to 13.5 μm below. The highest average microhardness in the top, middle and bottom areas obtained by using the interpass milling depth of 300 μm were 369 HV 0.2 , 371 HV 0.2 and 371 HV 0.2 respectively, which was increased by 32 HV 0.2 , 28 HV 0.2 and 26 HV 0.2 compared with non-interpass milling respectively. The horizontal and vertical ultimate tensile strength first increases and then decreases with the increase of interpass milling depth, reaching its maximum at a milling depth of 300 μm. The highest tensile strength of the horizontal and vertical directions obtained by using the interpass milling depth of 300 μm were 1022 MPa and 1042 MPa. The level of the ultimate tensile strength is related to the combined proportion of total average β grain size and total average <15 μm α phase size, and the proportion of both is balanced and maximized to obtain the maximum ultimate tensile strength. The interpass milling depth of 300 μm satisfies both conditions, so its maximum horizontal and vertical ultimate tensile strength is achieved. Fracture type of tensile specimen was ductile fracture due to observing a lot of dimples on the fracture morphology. The above conclusions show that interpass milling is an aided process to effectively improve the microstructure and mechanical properties of TC4 titanium alloy GTAW wire arc additive manufacturing thin-walled parts, which has high research significance and practical value.

Effect of Diameter and Content of Zirconium Dioxide on the Microstructure and Mechanical Properties of the TC17 Titanium Alloy Repaired by Wire Arc Additive Manufacture

Effects of Zr Addition on the Deformation Behavior, Microstructure and Mechanical Properties of Dental Ti Alloys

Effects of Trace Sn and Cr Addition on Microstructure and Mechanical Properties of TC17 Titanium Alloy Repaired by Wire Arc Additive Manufacturing

Effects of Thermal Undercooling and Thermal Cycles on the Grain and Microstructure Evolution of TC17 Titanium Alloy Repaired by Wire Arc Additive Manufacturing

Microstructure and Mechanical Properties of Wire Arc Additive Repairing Ti–5Al–2Sn–2Zr–4Mo–4Cr Titanium Alloy

Effects of trace boron addition and different arc types on microstructure and mechanical properties of TC11/TC17 dual alloy fabricated by wire arc additive manufacturing

Microstructural Characteristics and Mechanical Properties of Repaired Titanium Alloy Blade by Arc Additive Manufacturing Process

Controlling the Microstructure and Properties of Ti-6.5al-2zr-1mo-1v Components Fabricated by High-Deposition-Rate Wire Arc Additive Manufacturing

Improvement of Microstructure and Mechanical Properties of TC4 Titanium Alloy GTAW based Wire Arc Additive Manufacturing by using Interpass Milling

A comparison on microstructure features, compression property and wear performance of TC4 and TC11 alloys fabricated by multi-wire arc additive manufacturing

Eliminating Microstructure and Mechanical Anisotropy of Ti-6.5Al-2Zr-1Mo-1 V Manufactured by Hot-Wire Arc Additive Manufacturing Through Boron Addition

Realization of synergistic enhancement for fracture strength and ductility by adding TiC particles in wire and arc additive manufacturing 2219 aluminium alloy

Research on high efficiency deposition method of titanium alloy based on double-hot-wire arc additive manufacturing and heat treatment

Integrated control mechanism of ultrasound and ZrO2 particles on differential microstructures for the wire arc additive manufacturing

Grain Refinement of Wire Arc Additive Manufactured Titanium Alloy by the Combined Method of Boron Addition and Low Frequency Pulse Arc

Effects of heat treatment combined with laser shock peening on wire and arc additive manufactured Ti17 titanium alloy: Microstructures, residual stress and mechanical properties

Integrated control mechanism of ultrasound and ZrO<sub>2</sub> particles on differential microstructures for the wire arc additive manufacturing

Contribution Made by Double-Sized TiC Particles Addition to the Ductility–strength Synergy in Wire and Arc Additively Manufactured Al–Cu Alloys

Mechanical and tribological characterization of wire and multi-wire arc additive manufactured thin-walled TC11 component

Fabrication of γ-TiAl intermetallic alloy using the twin-wire plasma arc additive manufacturing process: Microstructure evolution and mechanical properties

Microstructure Modification of Twin-Wire Directed Energy Deposition-Arc Fabricated Γ-Tial Alloy Via Deposition Current Control