Abstract:TC4 titanium alloy wire arc additive manufacturing (WAAM) is easy to produce coarse columnar β grain structure which affects mechanical properties. So in this paper, an innovative process of interpass milling assisted TC4 titanium alloy gas tungsten arc welding (GTAW) WAAM is proposed. The controlling interpass milling depth is used to improve the microstructure and mechanical properties of TC4 titanium alloy parts during the GTAW-WAAM. The results showed that the coarse columnar β grains and fine α phase were observed in the non-interpass milling part. When the interpass milling assistance GTAW-WAAM was employed, the coarse columnar β grains transformed into short columnar and equiaxed grains. With the increased of interpass milling depth, the average size of α phase was gradually refined to 13.5 μm below. The highest average microhardness in the top, middle and bottom areas obtained by using the interpass milling depth of 300 μm were 369 HV 0.2 , 371 HV 0.2 and 371 HV 0.2 respectively, which was increased by 32 HV 0.2 , 28 HV 0.2 and 26 HV 0.2 compared with non-interpass milling respectively. The horizontal and vertical ultimate tensile strength first increases and then decreases with the increase of interpass milling depth, reaching its maximum at a milling depth of 300 μm. The highest tensile strength of the horizontal and vertical directions obtained by using the interpass milling depth of 300 μm were 1022 MPa and 1042 MPa. The level of the ultimate tensile strength is related to the combined proportion of total average β grain size and total average <15 μm α phase size, and the proportion of both is balanced and maximized to obtain the maximum ultimate tensile strength. The interpass milling depth of 300 μm satisfies both conditions, so its maximum horizontal and vertical ultimate tensile strength is achieved. Fracture type of tensile specimen was ductile fracture due to observing a lot of dimples on the fracture morphology. The above conclusions show that interpass milling is an aided process to effectively improve the microstructure and mechanical properties of TC4 titanium alloy GTAW wire arc additive manufacturing thin-walled parts, which has high research significance and practical value.

Grain Refinement of Wire Arc Additive Manufactured Titanium Alloy by the Combined Method of Boron Addition and Low Frequency Pulse Arc

Grain Morphology Evolution Mechanism of Titanium Alloy by the Combination of Pulsed Arc and Solution Element During Wire Arc Additive Manufacturing

Enhanced High-Temperature Strength and Ductility of Wire Arc Additive Manufactured Al-Ce-Mg Alloys with Fine Α-Al/al11ce3 Eutectics

Impact of Process Parameters on Forming Quality and Deposition Efficiency of Unsupported Rods in Wire Arc Additive Manufacturing

Grain Morphology Evolution and Texture Characterization of Wire and Arc Additive Manufactured Ti-6Al-4V

Understanding the grain refinement mechanisms in aluminium 2319 alloy produced by wire arc additive manufacturing

Weakening the Anisotropic Property and Refining Prior-β Grains via Hammer Peening Treatment During Wire Arc Additively Manufacturing of Ti-6Al-4V

Achieving a Columnar-to-Equiaxed Transition Through Dendrite Twinning in High Deposition Rate Additively Manufactured Titanium Alloys

Hierarchical Grain Refinement During the Laser Additive Manufacturing of Ti-6Al-4V Alloys by the Addition of Micron-Sized Refractory Particles

Controlling the Microstructure and Properties of Ti-6.5al-2zr-1mo-1v Components Fabricated by High-Deposition-Rate Wire Arc Additive Manufacturing

Grain refining of Ti-6Al-4V alloy fabricated by laser and wire additive manufacturing assisted with ultrasonic vibration

Grain refinement and mechanical properties improvement of Inconel 625 alloy fabricated by ultrasonic-assisted wire and arc additive manufacturing

Grain refinement in unalloyed tantalum structure deposited using Wire + Arc Additive Manufacture and vertical cold rolling

Effects of trace boron addition and different arc types on microstructure and mechanical properties of TC11/TC17 dual alloy fabricated by wire arc additive manufacturing

Improvement of Microstructure and Mechanical Properties of TC4 Titanium Alloy GTAW based Wire Arc Additive Manufacturing by using Interpass Milling

Achieving high ductility in a selectively laser melted commercial pure-titanium via in-situ grain refinement

A New Method for Refinement of Ti-6Al-4 V Prior-Β Grain Structure in the Alternating Magnetic Field Assisted Narrow Gap Gas Tungsten Arc Welding (AMF-GTAW) Via Filler Wire Oscillation

Microstructure regulation of titanium alloy functionally gradient materials fabricated by alternating current assisted wire arc additive manufacturing

Effects of heat treatment combined with laser shock peening on wire and arc additive manufactured Ti17 titanium alloy: Microstructures, residual stress and mechanical properties

Mathematical analysis and process optimization of wire and arc additive manufactured Ti6Al4V ELI alloy with in-situ rolling

Promoting the columnar to equiaxed transition and grain refinement of titanium alloys during additive manufacturing