Effect of Cu content on microstructure and properties of Ti-6Al-4V alloy fabricated by double-wire arc additive manufacturing
Yinbao Tian,Zhetao Liang,Guoyang Zhang,Hongqiang Liu,Zhengyi Jiang,Xin Zhang,Jingling Wang,Jian Han,Xiaoxin Zhao
DOI: https://doi.org/10.1016/j.mtcomm.2024.109393
IF: 3.8
2024-06-04
Materials Today Communications
Abstract:To solve the formation of coarse columnar β grains from Ti-6Al-4 V parts fabricated by wire + arc additive manufacturing, this study adds Cu element for in-situ alloying, effectively suppressing the growth of columnar grains and further enhancing properties. The results show that an addition of Cu element suppresses the lateral growth of β grains, eliminating the columnar structure of β grains. Compared with the Ti-6Al-4 V component, the original β grains in the Ti-6Al-4 V-10Cu component exhibit a refinement of 96 %. With an increase of Cu content, the phase structure of α-Ti transitions from lamellar to needle-like and eventually to equiaxed crystal structure. Moreover, as the Cu content rises, the precipitation of Ti 2 Cu increases, leading to precipitation strengthening and enhancing the microhardness. The average strength of the Ti-6Al-4 V-10Cu, Ti-6Al-4 V-11.7Cu, and Ti-6Al-4 V-15.7Cu walls is increased by 35.5 %, 56.9 %, and 71.6 %, respectively, compared with the Ti-6Al-4 V wall. The ultimate tensile strength is enhanced by 34.9 %, 49.5 %, and −1.4 %, respectively. However, the elongation is reduced by 48.6 %, 63.2 %, and 75.6 %, respectively.
materials science, multidisciplinary