Abstract:Wire arc additive manufacturing (WAAM) technology has potential advantages in the production of large-scale aluminum alloy components. However, as-deposited Al–Cu alloys produced by WAAM often suffer from porosity defects and coarse eutectic phases distributed along the grain boundaries, resulting in poor mechanical properties and hindering the applicability of WAAM to prepare aluminum alloy components. Herein, 2219 aluminum alloy was prepared using WAAM assisted by interlayer friction stir processing (FSP). Porosity defects in the as-deposited materials were eliminated, and coarse eutectic phases were broken and dissolved into the α-Al matrix via interlayer FSP, improving the mechanical properties of the components. The specimens processed by WAAM + interlayer FSP were subjected to different thermal cycling at different locations. The top-layer stir zone (SZ) was not affected by thermal cycling during the additive manufacturing process, and mechanical properties in the SZ were superior to those in the middle region. Compared with the as-deposited materials prepared by WAAM, the yield strength (YS) and ultimate tensile strength (UTS) in the middle region along the horizontal direction of the components manufactured by WAAM + interlayer FSP increased from 118 to 143 MPa and from 255 to 277 MPa, respectively. Further, the ultimate fatigue strength increased from 97 to 139 MPa. The YS and UTS along the vertical direction were 140 and 268 MPa, respectively, which are slightly lower than those along the horizontal direction. This is due to the small overlapping between the two adjacent SZs. The partially melted zone (PMZ) between the SZs was not completely eliminated, and the θ phase in the PMZ was mostly distributed along the grain boundaries.

Microstructure, texture and mechanical properties of Inconel GH4169 superalloy fabricated by wire arc additive manufacturing with arc oscillation

Impact of Process Parameters on Forming Quality and Deposition Efficiency of Unsupported Rods in Wire Arc Additive Manufacturing

Microstructure and Mechanical Properties of 304L Steel Fabricated by Arc Additive Manufacturing

Effect of arc oscillation on porosity and mechanical properties of 2319 aluminum alloy fabricated by CMT-wire arc additive manufacturing

Effects of synchronized magnetic arc oscillation on microstructure, texture, grain boundary and mechanical properties of wire arc additively manufactured Ti6Al4V alloy

Microstructure and Mechanical Properties of Thick‐Walled Inconel 625 Alloy Manufactured by Wire Arc Additive Manufacture with Different Torch Paths

Microstructure evolution and mechanical properties of the wire + arc additive manufacturing Al-Cu alloy

Evolution of microstructure and properties in 2219 aluminum alloy produced by wire arc additive manufacturing assisted by interlayer friction stir processing

Wire Oscillating Laser Additive Manufacturing of 2319 Aluminum Alloy: Optimization of Process Parameters, Microstructure, and Mechanical Properties

Investigate the effect of arc characteristic on the mechanical properties of 5A56 Al alloy in CMT arc additive manufacturing

Effect of Deposition Strategies on Microstructures, Defects and Mechanical Properties of 5356 Aluminum Alloy by Wire Arc Additive Manufacturing

Microstructure and Mechanical Properties of Low-Carbon High-Strength Steel Fabricated by Wire and Arc Additive Manufacturing

Minimizing porosity and optimizing microstructure of hot-wire arc additive manufactured Al-Cu-Mg-Ag alloy for strength increment

Grain refinement and mechanical properties improvement of Inconel 625 alloy fabricated by ultrasonic-assisted wire and arc additive manufacturing

Microstructural modification and enhanced mechanical properties of wire-arc additive manufactured 6061 aluminum alloy via interlayer friction stir processing

The effects of ultrasonic frequency pulsed arc on wire + arc additively manufactured high strength aluminum alloys

Microstructural and Defect Evolution during WAAM Resulting in Mechanical Property Differences for AA5356 Component

Effects of Location on the Microstructure and Mechanical Properties of Cu-8Al-2Ni-2Fe-2Mn Alloy Produced Through Wire Arc Additive Manufacturing

Wire arc additive manufacturing of Al-Zn-Mg-Cu alloy: Microstructures and mechanical properties

Microstructural development during wire arc additive manufacturing of copper-based components

Microstructure refinement and mechanical properties enhancement of wire-arc additive manufactured 2219 aluminum alloy assisted by interlayer friction stir processing