Abstract:TC4 titanium alloy wire arc additive manufacturing (WAAM) is easy to produce coarse columnar β grain structure which affects mechanical properties. So in this paper, an innovative process of interpass milling assisted TC4 titanium alloy gas tungsten arc welding (GTAW) WAAM is proposed. The controlling interpass milling depth is used to improve the microstructure and mechanical properties of TC4 titanium alloy parts during the GTAW-WAAM. The results showed that the coarse columnar β grains and fine α phase were observed in the non-interpass milling part. When the interpass milling assistance GTAW-WAAM was employed, the coarse columnar β grains transformed into short columnar and equiaxed grains. With the increased of interpass milling depth, the average size of α phase was gradually refined to 13.5 μm below. The highest average microhardness in the top, middle and bottom areas obtained by using the interpass milling depth of 300 μm were 369 HV 0.2 , 371 HV 0.2 and 371 HV 0.2 respectively, which was increased by 32 HV 0.2 , 28 HV 0.2 and 26 HV 0.2 compared with non-interpass milling respectively. The horizontal and vertical ultimate tensile strength first increases and then decreases with the increase of interpass milling depth, reaching its maximum at a milling depth of 300 μm. The highest tensile strength of the horizontal and vertical directions obtained by using the interpass milling depth of 300 μm were 1022 MPa and 1042 MPa. The level of the ultimate tensile strength is related to the combined proportion of total average β grain size and total average <15 μm α phase size, and the proportion of both is balanced and maximized to obtain the maximum ultimate tensile strength. The interpass milling depth of 300 μm satisfies both conditions, so its maximum horizontal and vertical ultimate tensile strength is achieved. Fracture type of tensile specimen was ductile fracture due to observing a lot of dimples on the fracture morphology. The above conclusions show that interpass milling is an aided process to effectively improve the microstructure and mechanical properties of TC4 titanium alloy GTAW wire arc additive manufacturing thin-walled parts, which has high research significance and practical value.

A New Method for Refinement of Ti-6Al-4 V Prior-Β Grain Structure in the Alternating Magnetic Field Assisted Narrow Gap Gas Tungsten Arc Welding (AMF-GTAW) Via Filler Wire Oscillation

Impact of Process Parameters on Forming Quality and Deposition Efficiency of Unsupported Rods in Wire Arc Additive Manufacturing

An Innovative Methodology in Narrow Gap GTAW for Alternating Magnetic Field with Synchronous Swing of Filler Wire and Arc

The wetting and stirring behavior of molten pool in narrow gap AMF-GTAW by numerical and experimental analysis

Research on Microstructure and Mechanical Properties of Square Wave Alternating Current Tungsten Inert Gas Welded Joints in 2219-T6 Aluminum Alloy

Study on arc shape, weldment microstructure, and mechanical properties of Ti-6Al-4V welded by FFDP TIG waveform

Improvement of Microstructure and Mechanical Properties of TC4 Titanium Alloy GTAW based Wire Arc Additive Manufacturing by using Interpass Milling

Stirring effect of the rotating arc on the molten pool during non-axisymmetric tungsten NG-GTAW

Energy reconstruction and metallurgical characteristics in 316L NG-LWFW with assisted wire wobbling by numerical and experimental analysis

Microstructural evolution and performance improvement mechanism of Ti-6Al-4V fabricated by Oscillating-Wire laser additive manufacturing

A novel approach to regulate energy allocation and melt flow in narrow gap laser welding with electromagnetic assisted wire wobbling

Fabrication of γ-TiAl intermetallic alloy using the twin-wire plasma arc additive manufacturing process: Microstructure evolution and mechanical properties

Weakening the Anisotropic Property and Refining Prior-β Grains via Hammer Peening Treatment During Wire Arc Additively Manufacturing of Ti-6Al-4V

Grain refining of Ti-6Al-4V alloy fabricated by laser and wire additive manufacturing assisted with ultrasonic vibration

Effect of pulse frequency on microstructure and properties of Ti-6Al-4V by ultrahigh-frequency pulse gas tungsten arc welding

Fabrication of Titanium Aluminide Alloys by Twin-Wire Tungsten Inert Gas Welding Applied with High-Frequency Induction Heating Wire Technology: Processing, Microstructure, and Properties

Short Circuiting Transfer, Formation, and Microstructure of Ti-6Al-4V Alloy by External Longitudinal Magnetic Field Hybrid Metal Inert Gas Welding Additive Manufacturing

Numerical simulation on molten pool behavior of narrow gap gas tungsten arc welding

Enhancing wire arc additive manufacturing in vibrational environments with longitudinal magnetic fields

Evolution of Precipitates in a Mechanical Vibration-Assisted Metal Inert Gas Welded Joint of 6082-T6 Aluminum Alloy Made with an ER5356 Filler Wire

Manipulating Molten Pool in In-Situ Additive Manufacturing of Ti-22Al-25 Nb Through Alternating Dual-Electron Beams