Abstract:Incorporated with the benefits of dynamic strain aging (DSA) and laser shock peening (LSP), warm laser shock peening (WLSP) is able to induce a compressive residual stress (CRS) layer with high thermal stability on the near-surface of the material. It has been widely used in recent years as a new surface modification technique to prolong the fatigue life of aero-engine turbine blades. Single WLSP has limited effect on material modification, while multiple WLSP when the confining layer is quartz glass will affect the thickness and thermal stability of the CRS layer during replacement of the confining layer, absorbing layer, and cooling and heating. To address this issue, this study investigates the mechanism of the CRS response, mechanism of strengthening, mechanism of action, and change of electrochemical corrosion performance of DD6 superalloy samples to different surface treatments after double LSP, single WLSP plus single LSP and double WLSP surface treatments by changing the experimental sequence of WLSP and LSP.The experimental results show that all three surface treatments deform the sample by inducing 110 cross-slip bands on the sample surface. Also all three surface treatments strengthen the sample surface by pipeline diffusion of elements to form a dislocation network similar to the gamma/gamma ' substructure. Meanwhile, single WLSP plus single LSP treatments can effectively prevent the thermal relaxation of the previously induced CRS layer.The final induced CRS layer thickness, dislocation distribution and dislocation density are better than those of double LSP and double WLSP. Pipeline diffusion of elements can improve the electrochemical and thermal corrosion resistance of the single-crystal superalloy.

The Effect of Warm Laser Shock Peening on the Thermal Stability of Compressive Residual Stress and the Hot Corrosion Resistance of Ni-based Single-Crystal Superalloy

An Investigation on the Effect of Change in Experimental Sequence of Warm Laser Shock Peening and Laser Shock Peening on the Performance of DD6 Nickel-Based Single-Crystal Superalloy

An Investigation of the Effect of Warm Laser Shock Peening on the Surface Modifications of [001]-Oriented DD6 Superalloy

Impact on Mechanical Properties and Microstructural Response of Nickel-Based Superalloy GH4169 Subjected to Warm Laser Shock Peening

Effect of Warm Laser Shock Peening on the Low-Cycle Fatigue Behavior of DD6 Nickel-Based Single-Crystal Superalloy

Effect of Laser Shock Peening on the Hot Corrosion Behavior of Ni-based Single-Crystal Superalloy at 750°C

Laser Shock Peening of GH4133 Nickel-based Superalloy

Thermal Evolutions of Residual Stress and Strain Hardening of GH4169 Ni-based Superalloy Treated by Laser Shock Peening

Thermal Stability of Laser Shock Peening Processed Ni-based Superalloy DZ17G

The Effects of Laser Shock Peening on Fatigue Life in Ni-Based Superalloy

Characteristics of microstructure evolution of surface treated IN718 superalloy by warm laser shock peening during long-term aging at high temperatures

Effect of Laser Shock Processing on Fatigue Life of Ni-based Superalloy

Research on Finite Element Simulation and Recrystallization of Laser Shock Peened Nickel-Based Single-Crystal Superalloy

Effects of laser shock processing on fatigue property of GH742 Ni-based superalloy

The effect of laser shock processing on the microstructures and properties of 2060 Al Li alloys

Surface strengthening and fatigue life improvement of single crystal Ni-based superalloys via laser shock peening without coating

Quantification of room temperature strengthening of laser shock peened Ni-based superalloy using synchrotron microdiffraction

Effect of laser shock peening on the tensile behavior and notch sensitivity of Ni-based single-crystal superalloy

Evolutions of microstructure, phase, microhardness, and residual stress of multiple laser shock peened Ni-based single crystal superalloy after short-term thermal exposure

Microstructural evolution and mechanical behaviors of Al-Cu-Li alloy processed by laser shock peening

On the Microstructure, Residual Stress and Fatigue Performance of Laser Metal Deposited TC17 Alloy Subjected to Laser Shock Peening