Abstract:Incorporated with the benefits of dynamic strain aging (DSA) and laser shock peening (LSP), warm laser shock peening (WLSP) is able to induce a compressive residual stress (CRS) layer with high thermal stability on the near-surface of the material. It has been widely used in recent years as a new surface modification technique to prolong the fatigue life of aero-engine turbine blades. Single WLSP has limited effect on material modification, while multiple WLSP when the confining layer is quartz glass will affect the thickness and thermal stability of the CRS layer during replacement of the confining layer, absorbing layer, and cooling and heating. To address this issue, this study investigates the mechanism of the CRS response, mechanism of strengthening, mechanism of action, and change of electrochemical corrosion performance of DD6 superalloy samples to different surface treatments after double LSP, single WLSP plus single LSP and double WLSP surface treatments by changing the experimental sequence of WLSP and LSP.The experimental results show that all three surface treatments deform the sample by inducing 110 cross-slip bands on the sample surface. Also all three surface treatments strengthen the sample surface by pipeline diffusion of elements to form a dislocation network similar to the gamma/gamma ' substructure. Meanwhile, single WLSP plus single LSP treatments can effectively prevent the thermal relaxation of the previously induced CRS layer.The final induced CRS layer thickness, dislocation distribution and dislocation density are better than those of double LSP and double WLSP. Pipeline diffusion of elements can improve the electrochemical and thermal corrosion resistance of the single-crystal superalloy.

Effect of Laser Shock Peening on the Hot Corrosion Behavior of Ni-based Single-Crystal Superalloy at 750°C

Effect of Microstructure Evolution and Phase Precipitations on Hot Corrosion Behavior of IN718 Alloy Subjected to Multiple Laser Shock Peening

The Effect of Warm Laser Shock Peening on the Thermal Stability of Compressive Residual Stress and the Hot Corrosion Resistance of Ni-based Single-Crystal Superalloy

Impact on Mechanical Properties and Microstructural Response of Nickel-Based Superalloy GH4169 Subjected to Warm Laser Shock Peening

Laser Shock Peening of GH4133 Nickel-based Superalloy

Effect of laser shock peening on the tensile behavior and notch sensitivity of Ni-based single-crystal superalloy

Effect of Laser Shock Processing on Fatigue Life of Ni-based Superalloy

The Effects of Laser Shock Peening on Fatigue Life in Ni-Based Superalloy

Effects of laser shock peening on the hot corrosion behaviour of the selective laser melted Ti6Al4V titanium alloy

Effects of laser shock processing on fatigue property of GH742 Ni-based superalloy

An Investigation on the Effect of Change in Experimental Sequence of Warm Laser Shock Peening and Laser Shock Peening on the Performance of DD6 Nickel-Based Single-Crystal Superalloy

Effect of Laser Shock Peening on Residual Stress, Microstructure and Hot Corrosion Behavior of Damage-Tolerant TC21 Titanium Alloy

Thermal Stability of Laser Shock Peening Processed Ni-based Superalloy DZ17G

Evolutions of microstructure, phase, microhardness, and residual stress of multiple laser shock peened Ni-based single crystal superalloy after short-term thermal exposure

Thermal Evolutions of Residual Stress and Strain Hardening of GH4169 Ni-based Superalloy Treated by Laser Shock Peening

Characteristics of microstructure evolution of surface treated IN718 superalloy by warm laser shock peening during long-term aging at high temperatures

Improvement of Fatigue Life of GH3039 Superalloy by Laser Shock Peening

The effect of laser shock processing on the microstructures and properties of 2060 Al Li alloys

An Investigation of the Effect of Warm Laser Shock Peening on the Surface Modifications of [001]-Oriented DD6 Superalloy

Laser Shock Processing of Ni-Base Superalloy and High Cycle Fatigue Properties

Comparison of surface integrity of GH4169 superalloy after high-energy, low-energy, and femtosecond laser shock peening