Abstract:Al0.6CoFeNi2V0.5 high entropy alloy was successfully designed and prepared via the nonconsumable arc-melting process, and it was annealed at 600 °C, 800 °C, and 1000 °C for 4 h. Its microstructure and mechanical properties were studied. The as-cast alloy consisted of FCC and BCC phases, and no phase transformation occurred during annealing at 600 °C. Hard Al3V-type metal compounds precipitated during annealing at 800 °C, and BCC particles precipitated in the FCC matrix during annealing at 1000 °C. After annealing, the strength and hardness of Al0.6CoFeNi2V0.5 high-entropy alloy both showed a decreasing trend, because the annealing process eliminated the internal stress in this alloy. However, as the annealing temperature increased, the strength and hardness of the Al0.6CoFeNi2V0.5 high-entropy alloy samples gradually increased. This is because the hard Al3V metal compounds precipitated when the annealing temperature was 800 °C, which produced the "second phase strengthening" effect. At 1000 °C, the larger volume fraction of the hard and fine BCC phase (21.81%) diffusely precipitated; the precipitation of this BCC phase not only produced a "second phase strengthening" effect, which also resulted in "solid solution strengthening", ultimately exhibiting enhanced hardness and strength. These findings have important theoretical reference value for the study of the microstructure and mechanical properties of high-entropy alloys. And, this study plays a significant role in promoting the research and development of new component materials that bear compressive loads, such as columns in large factory buildings, supports for cranes, and clamping bolts for rolling mills in practical mechanical engineering.

Effect of Aluminium Content on Microstrure and Mechanical Properties of AlxCoFe1.9Ni2.1 High Entropy Alloys

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Effects of Al Addition on Microstructure and Mechanical Properties of Alxcocrfeni High-Entropy Alloy

Microstructure and corrosion properties of AlxCuFeNiCoCr(x = 0.5, 1.0, 1.5, 2.0) high entropy alloys with Al content

Microstructure and Properties of Multi-Component AlxCoCrFeNiTi0.5 High-Entropy Alloys

Effect of Aluminum Content on Microstructure and Mechanical Properties of Al X CoCrFeMo0.5Ni High-Entropy Alloys

Effect of Al content on microstructure and mechanical properties of as-cast AlxFeMnNiCrCu0.5 high-entropy alloys

Study on Microstructure Evolution and Mechanical Properties of CoCrFeNiTiAlx High Entropy Alloys

Study on strength and toughness of FeCoCrNiAlx high entropy alloy

Microstructure and Mechanical Properties of AlxCoCrCuFeNi Multi-element High Entropy Alloy

Effects of Fe Content on Microstructures and Properties of AlCoCrFe X Ni High-Entropy Alloys

Effects of Al Addition on the Microstructure and Mechanical Property of AlxCoCrFeNi High-Entropy Alloys

Effect of Aluminum Content on Microstructure and Wear Resistance of CuCrFeMnTiAl_x High-Entropy Alloy

Effect of Al content on microstructure and wear properties of FeCrNiMnAlx high-entropy alloys

Effects of Cu addition on the microstructure and mechanical properties of AlFeCrCoTiCu x high-entropy alloys

Effect of Al content on the microstructure and properties of CoCrCuFeNiMoAlx high entropy alloy

The Effect of Heat Treatment on the Microstructure and Mechanical Properties of Al0.6CoFeNi2V0.5 High Entropy Alloy

Influence of increasing Al concentration on phase, microstructure and mechanical behaviors of Ni1.5CoFeCu1−xAlxV0.5 high entropy alloys

Evolution of Microstructure and Mechanical Properties of As-Cast Al x CrFe 2 Ni 2 High-Entropy Alloys with Al Content

Effect of Al Addition on Microstructures and Mechanical Properties of AlxCrFeNi2.5Mo High Entropy Alloys