Abstract:The CoCrFeNiAl high-entropy alloy, with varying Al compositions, was utilized as the bonding phase in this study to fabricate WC-10%CoCrFeNiAl x (where x represents the mole ratio of Al element, ranging from 0 to 1) hard alloys using the Spark Plasma Sintering method. The investigation focused on elucidating the influence mechanism of microstructure and properties of CoCrFeNiAl x high-entropy alloys on the mechanical properties of WC-10%CoCrFeNiAl x hard alloys. Isothermal oxidation testing was subsequently conducted to examine the impact of Al content on the high-temperature oxidation resistance of WC-10%CoCrFeNiAl x hard alloys. Finally, a comparison was made between the mechanical properties and high temperature oxidation resistance of WC-10%CoCrFeNiAl x hard alloys and conventional WC-6Co cemented carbide. The findings suggest that as the Al content increases, the CoCrFeNiAl x high-entropy alloy undergoes a transition from a single Face-Centered Cubic (FCC) phase to a combination of FCC and Body Centered Cubic (BCC) phases, ultimately transforming into a BCC phase. This evolution results in a gradual enhancement in hardness. The mechanical properties of WC-10CoCrFeNi hard alloy exhibit exceptional characteristics when the Al content is eliminated, with hardness, fracture toughness, and bending strength reaching 1702 MPa, 13.0 MPa·m 1/2 , and 1378 MPa respectively. As the Al content increases in WC-10%CoCrFeNiAl x hard alloys, there is a corresponding increase in hardness while fracture toughness and bending strength gradually decrease. Furthermore, an enhancement in high temperature oxidation resistance is observed. Finally, in comparison to the conventional WC-6Co hard alloy, the mechanical properties of WC-10CoCrFeNiAl x hard alloys exhibit similarity while demonstrating a significant enhancement in oxidation resistance.

Effect of Al content on the microstructure and properties of CoCrCuFeNiMoAlx high entropy alloy

Effect of Al Elements on the Microstructure and Properties of CoCrNiCuMoAlx High-Entropy Alloys

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Effect of Aluminum Content on Microstructure and Wear Resistance of CuCrFeMnTiAl_x High-Entropy Alloy

Effect of Al on Characterization and Properties of AlxCoCrFeNi High Entropy Alloy Prepared Via Electro-Deoxidization of the Metal Oxides and Vacuum Hot Pressing Sintering Process

Effects of Al Addition on Microstructure and Mechanical Properties of Alxcocrfeni High-Entropy Alloy

Microstructure and corrosion properties of AlxCuFeNiCoCr(x = 0.5, 1.0, 1.5, 2.0) high entropy alloys with Al content

Effect of Al content in CoCrFeNiAl x HEA on mechanical properties and high temperature oxidation resistance of WC-10%CoCrFeNiAl x hard alloy

Effect of Aluminium Content on Microstrure and Mechanical Properties of AlxCoFe1.9Ni2.1 High Entropy Alloys

Microstructure and Mechanical Properties of AlxCoCrCuFeNi Multi-element High Entropy Alloy

Mechanical Properties and Corrosion Resistance of AlxCoCuFeMn High-Entropy Alloys

Microstructure Evolution and Compressive Property Variation of CoCrFeNiAlx High Entropy Alloys Produced by Directional Solidification

Effect of Co Content on the Microstructure and Corrosion Behavior of Al0.3CoxCrFeNi High Entropy Alloys

Effect of Al content on microstructure, mechanical and corrosion properties of (Fe33Cr36Ni15Co15Ti1)100−x Al x high entropy alloys

Effect of Al content on microstructure and wear properties of FeCrNiMnAlx high-entropy alloys

Mechanical properties and water vapour corrosion behaviour of Al x CoCrFeNi high-entropy alloys

Effects of Al Addition on the Microstructure and Mechanical Property of AlxCoCrFeNi High-Entropy Alloys

Effects of Cu addition on the microstructure and mechanical properties of AlFeCrCoTiCu x high-entropy alloys

Effect of Al Addition on Microstructures and Mechanical Properties of AlxCrFeNi2.5Mo High Entropy Alloys

Effects of Al Addition on Structural Evolution and Tensile Properties of the FeCoNiCrMn High-Entropy Alloy System

Microstructure, Mechanical and Corrosion Properties of Co- and Cu-free AlxCrFeNi2.5Mo1-x High Entropy Alloys