Abstract:The CoCrFeNiAl high-entropy alloy, with varying Al compositions, was utilized as the bonding phase in this study to fabricate WC-10%CoCrFeNiAl x (where x represents the mole ratio of Al element, ranging from 0 to 1) hard alloys using the Spark Plasma Sintering method. The investigation focused on elucidating the influence mechanism of microstructure and properties of CoCrFeNiAl x high-entropy alloys on the mechanical properties of WC-10%CoCrFeNiAl x hard alloys. Isothermal oxidation testing was subsequently conducted to examine the impact of Al content on the high-temperature oxidation resistance of WC-10%CoCrFeNiAl x hard alloys. Finally, a comparison was made between the mechanical properties and high temperature oxidation resistance of WC-10%CoCrFeNiAl x hard alloys and conventional WC-6Co cemented carbide. The findings suggest that as the Al content increases, the CoCrFeNiAl x high-entropy alloy undergoes a transition from a single Face-Centered Cubic (FCC) phase to a combination of FCC and Body Centered Cubic (BCC) phases, ultimately transforming into a BCC phase. This evolution results in a gradual enhancement in hardness. The mechanical properties of WC-10CoCrFeNi hard alloy exhibit exceptional characteristics when the Al content is eliminated, with hardness, fracture toughness, and bending strength reaching 1702 MPa, 13.0 MPa·m 1/2 , and 1378 MPa respectively. As the Al content increases in WC-10%CoCrFeNiAl x hard alloys, there is a corresponding increase in hardness while fracture toughness and bending strength gradually decrease. Furthermore, an enhancement in high temperature oxidation resistance is observed. Finally, in comparison to the conventional WC-6Co hard alloy, the mechanical properties of WC-10CoCrFeNiAl x hard alloys exhibit similarity while demonstrating a significant enhancement in oxidation resistance.

Effect of Al content on microstructure and mechanical properties of as-cast AlxFeMnNiCrCu0.5 high-entropy alloys

Effect of Al content on microstructure and wear properties of FeCrNiMnAlx high-entropy alloys

Effect of Aluminum Content on Microstructure and Mechanical Properties of Al X CoCrFeMo0.5Ni High-Entropy Alloys

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Effects of Al Addition on Microstructure and Mechanical Properties of Alxcocrfeni High-Entropy Alloy

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Microstructural Evolution and Mechanical Properties of Al0.3CoCrFeNiSix. High-Entropy Alloys Containing Coherent Nanometer-Scaled Precipitates

Effects of Al Addition on the Microstructure and Mechanical Property of AlxCoCrFeNi High-Entropy Alloys

Enhancing the Strength of AlCrFeNi HEAs Via Tailoring Aluminum Content and Optimal Aging Treatment

Effect of Al content on microstructure, mechanical and corrosion properties of (Fe33Cr36Ni15Co15Ti1)100−x Al x high entropy alloys

Effect of Al/Ni ratio on phase, microstructure and mechanical properties of the Al CrFeMnNi2- high entropy alloys

Effect of Al Elements on the Microstructure and Properties of CoCrNiCuMoAlx High-Entropy Alloys

The Effect of Heat Treatment on the Microstructure and Mechanical Properties of Al0.6CoFeNi2V0.5 High Entropy Alloy

Effect of Al content on the microstructure and properties of CoCrCuFeNiMoAlx high entropy alloy

Effect of Al addition on the microstructures and deformation behaviors of non-equiatomic FeMnCoCr metastable high entropy alloys

Effect of Al content in CoCrFeNiAl x HEA on mechanical properties and high temperature oxidation resistance of WC-10%CoCrFeNiAl x hard alloy

Microstructure and Properties of Non-Equiatomic Ni10Cr6WFe9TiAlx High-Entropy Alloys Combined with High Strength and Toughness

Microstructures and properties of Fe1.25CoNi1.25CrxAl0.25 high-entropy alloys after cold-rolling and annealing

Nano-Structure Evolution and Mechanical Properties of AlxCoCrFeNi2.1 (x = 0, 0.3, 0.7, 1.0, 1.3) High-Entropy Alloy Prepared by Mechanical Alloying and Spark Plasma Sintering

Microstructure, Mechanical Properties, and Damping Capacity of AlxCoCrFeNi High-Entropy Alloys Prepared by Spark Plasma Sintering

Effect of element V on the as-cast microstructure and mechanical properties of Al0.4Co0.5VxFeNi high entropy alloys