Abstract:The as-cast microstructure characteristic and room temperature mechanical properties of Al0.4Co0.5VxFeNi high-entropy alloys (HEAs, where x = 0, 0.2, 0.4, and 0.6 in molar ratio, denoted as AC0, AC1, AC2, and AC3, respectively), fabricated by the vacuum arc melting method, were investigated by a combination of optical microscopy, scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and tension and compression tests. The vertical section of phase diagrams of Al0.4Co0.5VxFeNi HEAs were calculated with the Pandat software to show the equilibrium phases in the alloys at varying temperatures. The results show that Al0.4Co0.5VxFeNi HEAs have dual-phase structures. AC0, AC1, and AC2 show a typical dendritic structure composed of dendritic and interdendritic phases. AC3 shows a typical dual-phase structure with the characteristics of a eutectic structure. The comprehensive performance of the Al0.4Co0.5VxFeNi HEAs is remarkably enhanced by vanadium alloying. AC0 has a microhardness of about 2.79–2.90 GPa, which is three times lower than that of AC3. With an increase of V from 0.4 to 0.6, the structure of FCC-L12 transforms into an FCC phase. The AC1and AC2 HEAs present excellent strength and ductility, with elongation of tension tests at break exceeding 30%. Compared to the tension strength of AC1 and AC2, the yield strength of AC3 increases distinctly and its ultimate strength of extension increases, which is in trade off elongation. The fractured surfaces of AC1 and AC2 are ductile fractures, but the fracture surface feature of AC3 is mainly trench-like microstructures. During tensile deformation, the FCC phase is stretched by ductile fracturing while the BCC-B2 phase shows barely deformed cleavage fracturing, which causes the FCC phase to become thinner and with protruding edges.

Influence of increasing Al concentration on phase, microstructure and mechanical behaviors of Ni1.5CoFeCu1−xAlxV0.5 high entropy alloys

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Microstructural Evolution and Mechanical Properties of Al0.3CoCrFeNiSix. High-Entropy Alloys Containing Coherent Nanometer-Scaled Precipitates

Enhancing the Strength of AlCrFeNi HEAs Via Tailoring Aluminum Content and Optimal Aging Treatment

Effect of Al content on microstructure and wear properties of FeCrNiMnAlx high-entropy alloys

Effects of Al Addition on Microstructure and Mechanical Properties of Alxcocrfeni High-Entropy Alloy

Nano-Structure Evolution and Mechanical Properties of AlxCoCrFeNi2.1 (x = 0, 0.3, 0.7, 1.0, 1.3) High-Entropy Alloy Prepared by Mechanical Alloying and Spark Plasma Sintering

Effect of Al addition on the microstructures and deformation behaviors of non-equiatomic FeMnCoCr metastable high entropy alloys

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Microstructure Evolution and Compressive Property Variation of CoCrFeNiAlx High Entropy Alloys Produced by Directional Solidification

Influence of V and Al in Enhancing the Strength and Ductility of Co-rich High-Entropy Alloys

Effect of Al/Ni ratio on phase, microstructure and mechanical properties of the Al CrFeMnNi2- high entropy alloys

Effect of element V on the as-cast microstructure and mechanical properties of Al0.4Co0.5VxFeNi high entropy alloys

Effect of Al content on microstructure and mechanical properties of as-cast AlxFeMnNiCrCu0.5 high-entropy alloys

Effects of Al Addition on the Microstructure and Mechanical Property of AlxCoCrFeNi High-Entropy Alloys

Effect of Al Elements on the Microstructure and Properties of CoCrNiCuMoAlx High-Entropy Alloys

Multiscale-phase-driven strength-ductility synergy in Fe3Cr2CoNiAlx high entropy alloys

Influence of Tungsten Content on Microstructural Evolution of Cobalt-Containing High-Entropy Alloy via Mechanical Alloying

A combinatorial assessment of microstructure and mechanical properties in AlCrCuFeNi2Vx concentrated alloys

Microstructure, Mechanical Properties, and Damping Capacity of AlxCoCrFeNi High-Entropy Alloys Prepared by Spark Plasma Sintering

Microstructure and Properties of Non-Equiatomic Ni10Cr6WFe9TiAlx High-Entropy Alloys Combined with High Strength and Toughness