Abstract:The as-cast microstructure characteristic and room temperature mechanical properties of Al0.4Co0.5VxFeNi high-entropy alloys (HEAs, where x = 0, 0.2, 0.4, and 0.6 in molar ratio, denoted as AC0, AC1, AC2, and AC3, respectively), fabricated by the vacuum arc melting method, were investigated by a combination of optical microscopy, scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and tension and compression tests. The vertical section of phase diagrams of Al0.4Co0.5VxFeNi HEAs were calculated with the Pandat software to show the equilibrium phases in the alloys at varying temperatures. The results show that Al0.4Co0.5VxFeNi HEAs have dual-phase structures. AC0, AC1, and AC2 show a typical dendritic structure composed of dendritic and interdendritic phases. AC3 shows a typical dual-phase structure with the characteristics of a eutectic structure. The comprehensive performance of the Al0.4Co0.5VxFeNi HEAs is remarkably enhanced by vanadium alloying. AC0 has a microhardness of about 2.79–2.90 GPa, which is three times lower than that of AC3. With an increase of V from 0.4 to 0.6, the structure of FCC-L12 transforms into an FCC phase. The AC1and AC2 HEAs present excellent strength and ductility, with elongation of tension tests at break exceeding 30%. Compared to the tension strength of AC1 and AC2, the yield strength of AC3 increases distinctly and its ultimate strength of extension increases, which is in trade off elongation. The fractured surfaces of AC1 and AC2 are ductile fractures, but the fracture surface feature of AC3 is mainly trench-like microstructures. During tensile deformation, the FCC phase is stretched by ductile fracturing while the BCC-B2 phase shows barely deformed cleavage fracturing, which causes the FCC phase to become thinner and with protruding edges.

A combinatorial assessment of microstructure and mechanical properties in AlCrCuFeNi2Vx concentrated alloys

Microstructural Evolution and Mechanical Properties of Al0.3CoCrFeNiSix. High-Entropy Alloys Containing Coherent Nanometer-Scaled Precipitates

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Enhancing the Strength of AlCrFeNi HEAs Via Tailoring Aluminum Content and Optimal Aging Treatment

Experimental and DFT Investigations of AlNbTiVZr High Entropy Alloys with Excellent Mechanical Properties

Effect of element V on the as-cast microstructure and mechanical properties of Al0.4Co0.5VxFeNi high entropy alloys

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Microstructure and mechanical properties of Al0.4Co0.5V0.6FeNi high-entropy alloys processed by homogenization treatment

Microstructure and Properties of Non-Equiatomic Ni10Cr6WFe9TiAlx High-Entropy Alloys Combined with High Strength and Toughness

Microstructure and tensile properties of Co-free Fe4CrNi(AlTi) high-entropy alloys

Influence of V and Al in Enhancing the Strength and Ductility of Co-rich High-Entropy Alloys

Variation of BCC/B2 coherent microstructure and resultant improvement in strength of Al0.7CrxFe3−xCoNi high-entropy alloys

Microstructural evolution and mechanical properties of novel nanoparticles strengthened CoCrFeNi based high entropy alloy

Effect of Alloying on Microstructure and Mechanical Properties of AlCoCrFeNi2.1 Eutectic High-Entropy Alloy

Effect of Al/Ni ratio on phase, microstructure and mechanical properties of the Al CrFeMnNi2- high entropy alloys

Preparation and effect of vanadium addition on the mechanical properties of CoCrFeNiVx high-entropy alloy

Multiscale-phase-driven strength-ductility synergy in Fe3Cr2CoNiAlx high entropy alloys

Microstructures and mechanical behavior of non-equiatomic Co29Cr29Fe29Ni13-V high-entropy alloys at room and cryogenic temperatures

Microstructure Evolution and Mechanical Properties of Ultra-Fine Grain AlCrFe2Ni2Wx High-Entropy Alloys

Microstructure and mechanical properties variation with Ni content in Al0.8CoCr0.6Fe0.7Nix (x = 1.1, 1.5, 1.8, 2.0) eutectic high-entropy alloy system

Microstructures and mechanical properties of the precipitation strengthened Al0.4Cr0.7FexNi2V0.2 high entropy alloys