Abstract:The as-cast microstructure characteristic and room temperature mechanical properties of Al0.4Co0.5VxFeNi high-entropy alloys (HEAs, where x = 0, 0.2, 0.4, and 0.6 in molar ratio, denoted as AC0, AC1, AC2, and AC3, respectively), fabricated by the vacuum arc melting method, were investigated by a combination of optical microscopy, scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and tension and compression tests. The vertical section of phase diagrams of Al0.4Co0.5VxFeNi HEAs were calculated with the Pandat software to show the equilibrium phases in the alloys at varying temperatures. The results show that Al0.4Co0.5VxFeNi HEAs have dual-phase structures. AC0, AC1, and AC2 show a typical dendritic structure composed of dendritic and interdendritic phases. AC3 shows a typical dual-phase structure with the characteristics of a eutectic structure. The comprehensive performance of the Al0.4Co0.5VxFeNi HEAs is remarkably enhanced by vanadium alloying. AC0 has a microhardness of about 2.79–2.90 GPa, which is three times lower than that of AC3. With an increase of V from 0.4 to 0.6, the structure of FCC-L12 transforms into an FCC phase. The AC1and AC2 HEAs present excellent strength and ductility, with elongation of tension tests at break exceeding 30%. Compared to the tension strength of AC1 and AC2, the yield strength of AC3 increases distinctly and its ultimate strength of extension increases, which is in trade off elongation. The fractured surfaces of AC1 and AC2 are ductile fractures, but the fracture surface feature of AC3 is mainly trench-like microstructures. During tensile deformation, the FCC phase is stretched by ductile fracturing while the BCC-B2 phase shows barely deformed cleavage fracturing, which causes the FCC phase to become thinner and with protruding edges.

Microstructure and mechanical properties of Al0.4Co0.5V0.6FeNi high-entropy alloys processed by homogenization treatment

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Microstructural Evolution and Mechanical Properties of Al0.3CoCrFeNiSix. High-Entropy Alloys Containing Coherent Nanometer-Scaled Precipitates

Study on Precipitation in (cocrfemnni)90al6ti4 High Entropy Alloy

Enhancing the Strength of AlCrFeNi HEAs Via Tailoring Aluminum Content and Optimal Aging Treatment

Effect of element V on the as-cast microstructure and mechanical properties of Al0.4Co0.5VxFeNi high entropy alloys

Effect of Heat Treatment on the Microstructure and Mechanical Properties of the Al0.6CoCrFeNi High-Entropy Alloy

Microstructure and tensile properties of Co-free Fe4CrNi(AlTi) high-entropy alloys

Microstructure and mechanical properties of CoCrFeNiTa high entropy alloy prepared by mechanical alloying and spark plasma sintering

Microstructure and Magnetic Properties of the FeCoNi(CuAl)0.8Ga0.06 High-Entropy Alloy During the Phase Transition

Fine tuning in-sync the mechanical and magnetic properties of FeCoNiAl0.25Mn0.25 high-entropy alloy through cold rolling and annealing treatment

Microstructural Evolution and Tensile Properties of Al0.3CoCrFeNi High-Entropy Alloy Associated with B2 Precipitates

Microstructural evolution and mechanical behavior of Co‐free (Fe40Ni30Cr20Al10)100‐x Ti x high‐entropy alloys

Mechanical properties and wear behaviors of FeCoNiCrMnTix high-entropy alloys manufactured by vacuum arc melting

Microstructure, Mechanical Properties, and Damping Capacity of AlxCoCrFeNi High-Entropy Alloys Prepared by Spark Plasma Sintering

Microstructures and properties of Fe1.25CoNi1.25CrxAl0.25 high-entropy alloys after cold-rolling and annealing

A combinatorial assessment of microstructure and mechanical properties in AlCrCuFeNi2Vx concentrated alloys

Microstructure and mechanical properties of Al-Fe-Co-Cr-Ni high entropy alloy fabricated via powder extrusion

Study on the Microstructure and Mechanical Properties of Non-Equimolar NiCoFeAlTi High Entropy Alloy Doped with Trace Elements

Realizing strength-ductility combination of Fe3.5Ni3.5Cr2MnAl0.7 high-entropy alloy via coherent dual-phase structure

Microstructure and Properties of Non-Equiatomic Ni10Cr6WFe9TiAlx High-Entropy Alloys Combined with High Strength and Toughness