Tiwen Lu,Tianbing He,Panpan Zhao,Kang Sun,Angelo F. Andreoli,Hongyu Chen,Weiping Chen,Zhiqiang Fu,Sergio Scudino
Abstract:In this study, the mechanical and magnetic properties of FeCoNiAl0.25Mn0.25 high-entropy alloy (HEA) were investigated by subjecting as-cast samples to cold rolling and annealing at different temperatures for 1 h. The as-cast and cold rolled HEAs show a single-phase face-centered cubic (FCC) structure. The annealing temperature has a noteworthy influence on the phase composition and microstructure of the cold rolled HEA, and the microstructural evolution is described as follows: heterogeneous microstructure with a FCC matrix and body-centered cubic (BCC) precipitates (750 ℃ and 850 ℃) → recrystallized microstructure with FCC matrix and BCC precipitates (950 ℃) → coarse grains with a single FCC phase (1050 ℃). Though the HEA annealed at 1050 ℃ has the best ductility and lowest coercivity, the yield strength is very low. A good combination of ductility and strength is found in the sample annealed at 850 ℃ (CR+HEA-850), whose microstructure is comprised of BCC precipitates, recrystallized FCC equiaxed grains and a few FCC hard-deformed lamellae. The heterogeneous structure of the CR+HEA-850 resulted in a strong back stress, which contributes to its good mechanical properties. The high yield strength came from the grain refinement, dislocation strengthening, Orowan effect, and twin boundaries. Additionally, its soft magnetic properties are also appealing, showing high saturated magnetization (112.4 emu/g) and good coercivity (8.7 Oe). Compared with the HEAs on other conditions in this study and those previously reported, the CR+HEA-850 displays an interesting combination of magnetic and mechanical performance, which offers a strategy towards a new generation of multifunctional high-entropy alloys.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is how to finely adjust the mechanical and magnetic properties of FeCoNiAl\(_{0.25}\)Mn\(_{0.25}\) high - entropy alloy through cold rolling and annealing treatment to achieve the best balance between the two. Specifically, the research objective is to explore the effects of different annealing temperatures on the alloy phase composition, microstructure, and its mechanical and magnetic properties, thereby developing a new type of multi - functional high - entropy alloy with excellent soft magnetic and mechanical properties.
### Background and Problems of the Paper
1. **Characteristics of High - Entropy Alloys (HEAs)**
- High - entropy alloys are composed of five or more elements in equal - molar or near - equal - molar proportions and have a single - phase solid - solution structure.
- These alloys exhibit many excellent mechanical properties, such as high strength and high ductility, high fracture toughness, and high - temperature strength.
- In addition, some high - entropy alloys also show special physical properties, such as soft magnetic properties and superconducting properties.
2. **Requirements for Soft Magnetic Materials**
- Soft magnetic materials have important applications in power generation, transmission, and electromagnetic devices.
- Commercial soft magnetic materials have some disadvantages, such as low thermal stability, limited size, and complex production processes.
3. **Potential of FeCoNi - based High - Entropy Alloys**
- Some FeCoNi - based high - entropy alloys show high saturation magnetization and low coercivity and have potential applications as soft magnetic materials.
- However, relatively few comprehensive studies on the mechanical and magnetic properties of these alloys have been carried out.
### Research Objectives
- **Explore the Influence of Annealing Treatment**: Treat the cold - rolled FeCoNiAl\(_{0.25}\)Mn\(_{0.25}\) high - entropy alloy at different annealing temperatures (750°C, 850°C, 950°C, and 1050°C) to study the changes in its phase composition, microstructure, and properties.
- **Achieve Performance Optimization**: Find a treatment method that can improve mechanical properties (especially the balance between yield strength and ductility) while maintaining good soft magnetic properties.
### Main Research Contents
- **Experimental Methods**
- Prepare FeCoNiAl\(_{0.25}\)Mn\(_{0.25}\) high - entropy alloy and carry out cold - rolling treatment.
- Anneal the cold - rolled samples at different temperatures for 1 hour.
- Use techniques such as scanning electron microscope (SEM), energy - dispersive spectrometer (EDS), electron back - scatter diffraction (EBSD), transmission electron microscope (TEM), and X - ray diffraction (XRD) to analyze the microstructure and phase composition of the samples.
- Conduct tensile tests and magnetic property tests to evaluate the mechanical and magnetic properties of the samples.
- **Results and Discussion**
- **Microstructure**: Samples at different annealing temperatures exhibit different microstructures. For example, the sample annealed at 850°C has an obvious heterogeneous structure, including recrystallized FCC equiaxed grains, a small amount of FCC hard - deformed lamellae, and BCC precipitates.
- **Mechanical Properties**: The sample annealed at 850°C shows good mechanical properties, with high yield strength and ductility.
- **Magnetic Properties**: The sample annealed at 850°C also shows excellent soft magnetic properties, with high saturation magnetization and low coercivity.
### Conclusion
By finely controlling the process parameters of cold - rolling and annealing treatment, the microstructure of FeCoNiAl\(_{0.25}\)Mn\(_{0.25}\) high - entropy alloy can be effectively adjusted, thereby optimizing its mechanical and magnetic properties. The sample annealed at 850°C has achieved a good balance between mechanical and magnetic properties, showing the potential for developing new multi - functional high - entropy alloys.