Abstract:This paper presents the degradation analysis of monocrystalline silicon modules (SM55, produced by Siemens Solar company in 1992) installed for 18 years in Shenzhen, China, in hothumid climatic conditions, less than 500 m from the sea. From the measurement of the electrical performance, the average power degradation and the median power degradation of the modules were 24.62 and 24.38, respectively, or 1.56 per year in average. The reduction of power output is mainly attributed to the decrease of the fill factor. Through electroluminescence imaging, the degradation of the fill factor was found to be due to an increase in series resistance of the modules caused by solder bond failure and the corrosion of the Ag electrodes. From material analysis, scanning electron microscope inspection and analysis by energy dispersive X-ray spectroscopy showed the presence of acetate at the surface of the cells. The observation of needles in the silver metallization is a hint that corrosion of the metal occurred over time, probably caused by acetic acid, which can be a product of hydrolysis within ethylene vinyl acetate. It was found that the chemical reaction rate of acetate exhibits strong temperature dependence, following a typical Arrhenius-type dependence with temperature, which can result over long-time exposure in the field in corrosion of Ag metal fingers with predominance in the center of the cells operating at a higher temperature. Electron microscope imaging of cross section of cells also showed the presence of cracks between the ribbons and the Ag fingers, which can be caused by the large mismatch in coefficient of thermal expansion between the Si wafers and the Cu ribbons. Over time, the formation of intermetallic compounds in the solder layer may have made the solder more brittle and more susceptible to cracks.

Analysis of the Electrochemical Reactions and Ions Migration for Crystalline Silicon Solar Module under High System Voltage

Origin of ions for crystalline silicon solar module under high system voltage

The Electrochemical Reactions in Crystalline Silicon Solar Modules

MD Simulation and Transport Property Analysis of Silicon in High-Temperature Molten Fluoride Salts Electrolyte

Diffusion and Drift of Sodium Ions in PID-affected Mono-Crystalline Silicon Solar Modules

Oxygen and Carbon Precipitation in Multicrystalline Solar Silicon

Mechanism Analysis of Potential-Induced Degradation of P-type Crystalline Si Solar Cells

Macroscopic Study on Current Transport Path in Front‐Side Contacts of Crystalline Silicon Solar Cells

Analysis of the Degradation of Monocrystalline Silicon Photovoltaic Modules After Long-Term Exposure for 18 Years in a Hot–Humid Climate in China

Correlations Between Electrochemical Ion Migration and Anomalous Device Behaviors in Perovskite Solar Cells

Understanding the Relationship Between Ion Migration and the Anomalous Hysteresis in High-Efficiency Perovskite Solar Cells: A Fresh Perspective from Halide Substitution

Electro-analytical investigation of potential induced degradation in mc-silicon solar cells: case of sodium ion induced inductive loop

Investigation Of The Relationship Between Reverse Current Of Crystalline Silicon Solar Cells And Conduction Of Bypass Diode

Analysis of the Thermal Stress for Combined Electrode of Soldered Crystalline Silicon Solar Cells under Temperature Field

A Fine Model of Power Degradation for Crystalline Silicon Solar Modules

Reassessment of silicon heterojunction cell performance under operating conditions

Electroplated Metallization Method For Crystalline Silicon Solar Cells

Revealing Surface and Interface Evolution of Molybdenum Nitride as Carrier-Selective Contacts for Crystalline Silicon Solar Cells

Study on the Thermal Stress Distribution of Crystalline Silicon Solar Cells in BIPV

Potential-induced Degradation: Recombination Behavior, Temperature Coefficients and Mismatch Losses in Crystalline Silicon Photovoltaic Power Plant

Degradation of crystalline silicon solar cell caused by lightning induced impulse surge