Abstract:To improve the casting quality as well as the casting efficiency during the casting process, the effect of the interaction of process parameters and system structural parameters on the shrinkage volume and efficiency of the casting was investigated in this paper by using the response surface method for the simulation prediction of A356 alloy sand casting. The relationship between variables and response (shrinkage volume, solidification time) was established by Box-Behnken Design with pouring temperature (650–710 °C), mold preheating temperature (200–300 °C), width/thickness ratio of cross-section of sprue (1.2–1.5), width/thickness ratio of inner sprue section (2–4) and length/diameter ratio of straight sprue (1.5–2.5) as variables by the response surface method. The results are then optimized, and the optimal solution is selected by the NSGA-II algorithm and TOPSIS method. The results show that the changes in the cavities of the optimized and improved pouring system enhance the flow of the metal fluid and make the filling more complete. The gentle cooling of temperature is conducive to heat dissipation and layer-by-layer sequential solidification, which can effectively eliminate the casting's internal shrinkage loosening and shrinkage holes defects, thus forming a dense casting with good performance. After solving the optimized parameters and improving the pouring system, the solidification time (integrated solidification time) was reduced from 129.24 to 88.10s, and the shrinkage volume was reduced from 9.68 to 4.06 cm 3 .

Optimization of Investment Casting Parameters for Reduction of Shrinkage Porosity in Nickel-Based Superalloy Castings by Taguchi Method

Optimization of investment casting process for K477 superalloy aero-engine turbine nozzle by simulation and experiment

Optimization of Centrifugal Casting Process Parameters by Taguchi Method to Reduce Shrinkage Porosity Ratio of K417 Superalloy

Process Optimization of Low-pressure Die Casting of Aluminum Alloy Wheel based on Taguchi Method

Optimization of low-pressure die casting process parameters for reduction of shrinkage porosity in ZL205A alloy casting using Taguchi method

Effect of Mold Dwell Time on Shrinkage Defects in Investment Casting of Superalloy Turbine Blade

Optimization of process parameters to improve dimensional accuracy of investment casting using Taguchi approach

Numerical Simulation and Optimization of Investment Casting for Complex Thin-walled Castings

Parameter Optimization of Al-5Mg-3Zn-1Cu Basin-Shaped Centrifugal Casting: Simulation and Experimental Verification

Optimization of Casting System Structure Based on Genetic Algorithm for A356 Casting Quality Prediction

Numerical Simulation and Process Optimization of Vacuum Investment Casting for Be–Al Alloys

Prediction method of shrinkage cavity and shrinkage porosity in solidification process under low-pressure casting

Process Parameter Effects on Solidification Behavior of the Superalloy During Investment Casting

Multi-scale Modeling of Solidification Process of Ni-based Superalloy Investment Castings

Effect of centrifugal casting process on mold filling and grain structure of K418B turbine guide

Modeling of Investment Casting of Ti48Al48Cr2Nb2 (at%) Alloy Air Rudder Skeleton

Numerical and Experimental Study of the Elimination of Shrinkage in Complex and Small Investment Castings Using Water Cooling Process

Research on numerical simulation of investment casting process for gamma titanium aluminide turbocharger

Physical Simulation of Investment Casting for GTD-222 Ni-based Superalloy Processed by Controlled Cooling Rates

Investment casting of nozzle guide vanes from nickel-based superalloys: part I – thermal calibration and porosity prediction

Modeling of Shrinkage Porosity (Hole) in Ti Alloy Castings in Vertical Centrifugal Field