Effect of Al Content on Microstructure, Thermal Conductivity, and Mechanical Properties of Mg–La–Al–Mn Alloys

Zhao Xingfeng,Li Zixin,Zhou Wenke,Li Dejiang,Qin Ming,Zeng Xiaoqin

DOI: https://doi.org/10.1557/s43578-021-00319-x

2021-01-01

Abstract:In this study, the microstructure, thermal conductivity, and mechanical properties of Mg–4La–xAl–0.5Mn (x = 0, 0.5, 1, 1.5, 2, and 2.5 wt%) alloys were investigated. As the Al content of the alloys increases, the continuous network Mg12La phase is gradually replaced by non-network Al–La phases. The types of Al–La phases depend on the Al content. When the Al content is relatively low, the alloy tends to form Al2La or Al53La22 phases; otherwise, it tends to form an Al11La3 phase. The concentration of the Al solute atoms in the α-Mg matrix increases gradually as the Al content increases. The thermal conductivity is very sensitive to the concentration of Al solute atoms. The thermal conductivity of high-pressure die cast Mg–4La–2.5Al–0.5Mn alloy is 106.5 W/(m·k) and its yield stress, tensile strength, and elongation are 149 MPa, 253 MPa, and 11.5%, respectively.