Abstract:A novel two‐step joining method was developed to join alumina ceramics for high‐temperature applications. Firstly, alumina ceramics were bonded using Al2O3 powder at 1550°C. Subsequently, the Dy2O3‐Al2O3‐SiO2 glass was infiltrated into the interlayer at 1450°C to obtain the alumina/alumina joints with dense composite interlayer composed by Al2O3, Dy2Si2O7, and few glass phase. The flexural strength of the joints at 1000°C reached about 90% of that of alumina ceramics under the same conditions. After the thermal cycles from room temperature to 1000°C for 50 times, there was no significant change in the flexural strength of the joints. In this work, a novel two‐step joining method was developed to join alumina ceramics for high‐temperature applications. First, alumina ceramics were bonded using Al2O3 powder at 1550°C. Subsequently, the Dy2O3–Al2O3–SiO2 glass was infiltrated into the interlayer at 1450°C to obtain the alumina/alumina joints with dense composite interlayer composed by Al2O3, Dy2Si2O7, and few glass phase. The content of Al2O3 in the composite interlayer reached 52.7%. As a result, the coefficient of thermal expansion mismatch between the interlayer and the alumina ceramic was reduced to only 2%. The flexural strength of the joints at room temperature was equivalent to that of the alumina ceramic. Furthermore, the flexural strength of the joints at 1000°C reached about 90% of that of alumina ceramics under the same conditions. After the thermal cycles from room temperature to 1000°C for 50 times, there was no significant change in the flexural strength of the joints.

Joining ZTA Ceramics by Using Whiskers Reinforced Borosilicate Glasses for High-Temperature Applications

Joining of Al2O3 to ZTA Using a B2O3–Al2O3–SiO2 Glass with In-Situ Precipitated Whiskers

Surface Synthesis of Aluminum Borate Whiskers on the ZTA Ceramics and Its Application to Joining

Joining of Al 2 O 3 by epitaxial growth of aluminum borate whiskers for high-temperature applications

Crystallization and Wetting Behavior of Bismuth–borate–zinc Glass and Its Application in Low Temperature Joining Alumina Ceramics

Microstructure and Strength of Al2o3/Al2o3 Joints Bonded with Zno-Al2o3-B2o3-Sio2 Glass-Ceramic

Joining MgAl2O4 ceramics using ZnO–Al2O3–SiO2 glass ceramic with precipitated ZnAl2O4

Characterization of ZTA Composite Ceramic/Ti6Al4V Alloy Joints Brazed by AgCu Filler Alloy Reinforced with One-Dimensional Al<sub>18</sub>B<sub>4</sub>O<sub>33</sub> Single Crystal

Novel two‐step method for joining alumina ceramic by using Al2O3 powder followed by glass infiltration

Joining of Al2O3 Ceramics at Low Temperature

Joining AlN ceramics by ZnO–Al2O3–B2O3–SiO2 (ZABS) glass-ceramic at low temperature

Fabrication and Characterisation of High-Performance Joints Made of ZrB2-SiC Ultra-High Temperature Ceramics

Microstructure Evolution and Bonding Mechanism of ZrO2 Ceramic and Ti-6Al-4V Alloy Joints Brazed by Bi2O3-B2O3-ZnO Glass Paste

Thermoplastic bonding of TiAl-based alloy and YSZ ceramic utilizing a Ni60Nb40 metallic glass as the filler metal

Brazing of Al2O3 Ceramics by Bi2O3-B2O3-ZnO Glass

Low-temperature Brazing of Alumina Ceramics with Bismuth-Borate Glass in Air

Bonding ZrB2-SiC-G Ceramics Using Modified Organic Adhesive for Engineering Applications at Ultra High Temperatures in Air

The Authors Declare that They Have No Known Competing Financial Interests or Personal Relationships that Could Have Appeared to Influence the Work Reported in this Paper

A New Method for Direct Welding of Alumina and Zirconia Ceramics by Ultrashort Pulse Laser for High Temperature Application

Brazing ZTA Ceramic and Ti6Al4V Alloy Directly in Air: Excellent Oxidation Resistance at 800 °C

Crystallization Behavior in Bi2O3-B2O3-ZnO Glass Braze and Its Application for Joining Ferrite Ceramics at a Relatively Low Temperature