Abstract:A novel two‐step joining method was developed to join alumina ceramics for high‐temperature applications. Firstly, alumina ceramics were bonded using Al2O3 powder at 1550°C. Subsequently, the Dy2O3‐Al2O3‐SiO2 glass was infiltrated into the interlayer at 1450°C to obtain the alumina/alumina joints with dense composite interlayer composed by Al2O3, Dy2Si2O7, and few glass phase. The flexural strength of the joints at 1000°C reached about 90% of that of alumina ceramics under the same conditions. After the thermal cycles from room temperature to 1000°C for 50 times, there was no significant change in the flexural strength of the joints. In this work, a novel two‐step joining method was developed to join alumina ceramics for high‐temperature applications. First, alumina ceramics were bonded using Al2O3 powder at 1550°C. Subsequently, the Dy2O3–Al2O3–SiO2 glass was infiltrated into the interlayer at 1450°C to obtain the alumina/alumina joints with dense composite interlayer composed by Al2O3, Dy2Si2O7, and few glass phase. The content of Al2O3 in the composite interlayer reached 52.7%. As a result, the coefficient of thermal expansion mismatch between the interlayer and the alumina ceramic was reduced to only 2%. The flexural strength of the joints at room temperature was equivalent to that of the alumina ceramic. Furthermore, the flexural strength of the joints at 1000°C reached about 90% of that of alumina ceramics under the same conditions. After the thermal cycles from room temperature to 1000°C for 50 times, there was no significant change in the flexural strength of the joints.

Alumina ceramics joined with screen-printed B2O3 by spark plasma sintering

Alumina joints brazed by screen-printed B4C–SiO2 in air

Microstructure Evolution of Alumina/Alumina Joint Bonded by Boron Oxide–Alumina Nonmetal Powder Interlayer

Joining of Al 2 O 3 by epitaxial growth of aluminum borate whiskers for high-temperature applications

Air-brazed Al2O3 Joint with a Novel Bismuth Glass

Bonding Mechanisms and Shear Properties of Alumina Ceramic/Stainless Steel Brazed Joint

Microstructure Evolution During Air Bonding of Al2O3 to Al2O3 Joints Using Bismuth–borate–zinc Glass

Ultrafast Ultrasonic-Assisted Joining of Bare Α-Alumina Ceramics Through Reaction Wetting by Aluminum Filler in Air

Low-temperature Brazing of Alumina Ceramics with Bismuth-Borate Glass in Air

Surface Synthesis of Aluminum Borate Whiskers on the ZTA Ceramics and Its Application to Joining

Novel two‐step method for joining alumina ceramic by using Al2O3 powder followed by glass infiltration

Microstructure and Strength of Al2o3/Al2o3 Joints Bonded with Zno-Al2o3-B2o3-Sio2 Glass-Ceramic

Synthesis, Microstructure and Mechanical Properties of a MoAlB Ceramic Prepared by Spark Plasma Sintering from Elemental Powders

Crystallization and Wetting Behavior of Bismuth–borate–zinc Glass and Its Application in Low Temperature Joining Alumina Ceramics

Joining of Al2O3 to ZTA Using a B2O3–Al2O3–SiO2 Glass with In-Situ Precipitated Whiskers

Joining Pre-Oxidized Dense Si3N4 to Porous Si3N4 with Β-Spodumene Based Glass-Ceramic Interlayer

Brazing of Al2O3 Ceramics by Bi2O3-B2O3-ZnO Glass

Fabrication of alumina ceramics with high flexural strength using stereolithography

Joining silicon nitride ceramics with ZrSi2-SiC composite filler by spark plasma sintering

Microstructure and Properties of Alumina Ceramics Prepared from Submicrometer Alumina Powder with MgO–ZrO2 Coated on Alumina Grain Surface

Microwave Joining Alumina Ceramics Using Al-Si Alloy Powders at Low Temperature