Intrinsic dielectric properties and lattice vibrational characteristics of single phase BaTiO 3 ceramic

Long Wang,Jiqing Lv,Feng Shi,Kaixin Song,Wen Lei,Huanfu Zhou,Ze-Ming Qi,Jing Wang

DOI: https://doi.org/10.1007/s10854-021-06866-7

2021-01-01

Abstract:A single phase BaTiO 3 ceramic was prepared by traditional solid-state sintering process at 1220 °C for 4 h. XRD analysis results show that the obtained sample is tetragonal phase BaTiO 3 , the space group belongs to P4mm (No. 99). Lattice vibrational characteristics of BaTiO 3 ceramic were revealed according to Raman and far-infrared spectroscopy. By fitting far infrared data with 4-P model, the dielectric constant ( ε r ) of BaTiO 3 ceramic is 20.0782, while its dielectric loss (tan δ ) is 19.9756 × 10 −4 . The peak at 181 cm −1 has the greatest impact on the dielectric constant and dielectric loss. The theoretical dielectric properties of BaTiO 3 ceramic were calculated by C–M and damping formulas, which ε r = 20.1030 and tan δ = 19.1672 × 10 −4 . However, the theoretical data are too far different from the tested data, which is because the asymmetrical structure inside the tetragonal phase BaTiO 3 generates spontaneously polarize along the C axis, forming a ferroelectric domain and resulting in an increase in the dielectric constants, and thus the dielectric loss also increases.