Abstract:SrO–BaO–B2O3–SiO2 glass-ceramics with a high dielectric constant and low dielectric loss were prepared. The influence of the SiO2/BaO ratio on the sintering behavior, crystallization behavior, and properties were systematically investigated. The results showed that the increasing amount of liquid phase from increasing the SiO2/BaO ratio promoted sintering, resulting in an initial decrease in the sintering activation energy. However, the viscosity of the liquid phase continued to increase, leading to an increase in the sintering temperature and sintering activation energy when the SiO2/BaO ratio reached 0.90. As the SiO2/BaO ratio increased, the fraction of the primary phase BaSi2Al2O8 increased, and its grains grew; the minor phase SrTiO3 was suppressed, resulting in changes in the properties of the glass-ceramics. The sample with a SiO2/BaO ratio of 0.69, which was sintered at 850 °C for 10 min, showed excellent properties: a coefficient of thermal expansion (CTE) of 10.63 × 10−6 K−1 (25–500 °C), a dielectric constant (ϵr) of 16.24 (1 MHz), a dielectric loss (tanδ) of 3.39 × 10−3 (1 MHz), a flexural strength of 138.80 MPa, and a quality loss of acid corrosion of 1.06 × 10−4 g mm−2. The results indicated that the SrO–BaO–B2O3–SiO2 glass-ceramics used in this study have great potential for low-temperature co-fired ceramics applications.

Effect of the Ba/Ti Ratio on the Microstructures and Dielectric Properties of Barium Titanate‐Based Glass–Ceramics

SiO2/Al2O3 ratio dependence of microstructures and dielectric properties in barium strontium titanate glass ceramics

Improvement in the Microstructures and Dielectric Properties of Barium Strontium Titanate Glass–Ceramics by AlF3/MnO2 Addition

Glass additive in barium titanate ceramics and its influence on electrical breakdown strength in relation with energy storage properties

Crystallization kinetics and dielectric properties of barium strontium titanate based glass–ceramics

The Effect of B2o3-Li2co3 Addition on Sintering Behavior and Dielectric Properties of Ba0.6sr0.4tio3 Ceramics

Effect of La2O3 Concentration on Electrical Properties of Barium Strontium Titanate Glass-Ceramics

The effect of TiO2 and B2O3 on sintering behavior and crystallization behavior of SrO–BaO–B2O3–SiO2 glass-ceramics

Phase development and dielectric properties of barium strontium titanate based glass ceramics

Microstructures and Dielectric Properties of (na0.5bi0.5)0.775ba0.225ti0.775sn0.225o3 Relaxor Ferroelectric with Bi2O3–B2O3–ZnO Glass Addition

Influence of Alf3 Concentration on Microstructures and Energy Storage Properties of Barium Strontium Titanate Glass Ceramics

Effects of MnO2 Concentration on Dielectric Properties of Barium Strontium Titanate Glass Ceramics

Dielectric characteristics and their field dependence of (Ba, Ca)TiO3 ceramics

Effect of SiO2/Al2O3 ratio on the structure and electrical properties of MgO–Al2O3–SiO2 glass-ceramics doped with TiO2

Low Temperature Sintering and Microwave Dielectric Properties of Ba4nd9.33ti18o54 Ceramics Doped with Crystallizable Glass

Effect of SnO2 concentration on the dielectric properties of BaTiO3-(Sr1-1.5xBix)TiO3 ceramics

Effect of SiO2/BaO ratio on sintering behavior, crystallization behavior, and properties of SrO–BaO–B2O3–SiO2 glass-ceramics

Low-Firing and Microwave Dielectric Properties of Ba2Ti9O20 with BaO–B2O3–ZnO Glass Addition

Effect of NiO and Al2O3 on the Curie temperature, microstructure, and dielectric properties of Ba0.5Sr0.5TiO3 ceramics

Effects of Nb/Co Ratio on the Dielectric Properties of BaTiO3-based X7R Ceramics

Synthesis and performance of tetragonal Ca2+ doped BaTiO3 fine powders