Abstract:In this work, the effects of Nb2O5 addition on the dielectric properties and phase formation of BaTiO3 were investigated. A core–shell structure was formed for Nb-doped BaTiO3 resulted from a low diffusivity of Nb5+ ions into BaTiO3 when grain growth was inhibited. In the case of 0.3–4.8 mol% Nb2O5 additions, two dielectric constant peaks were observed. The Curie dielectric peak was determined by the ferroelectric-paraelectric transition of grain core, whereas the secondary broad peak at lower temperature was due to strong chemical inhomogeneity in Nb-doped BaTiO3 ceramics. The dielectric constant peak at Curie temperature was markedly depressed with the addition of Nb2O5. On the other hand, the secondary dielectric constant peak was enhanced when sintered above 1280 °C for higher Nb2O5 concentrations (≥1.2 mol%). The Curie temperature was shifted to higher temperatures, whereas the transition temperature corresponding to the secondary peak moved to lower temperatures as increasing the amount of Nb2O5 more than 1.2 mol%. The decrease of this lower transition temperature was assumed to be closely related with the secondary phase formation when Nb concentration greater than 1.2 mol%. From XRD analyses, a large amount of secondary phases was observed when Nb2O5 amount exceeded 1.2 mol%. The coefficients of thermal expansion of Nb-doped BaTiO3 were increased with increasing Nb2O5 contents, resulting in large internal stress between cores and shells. Therefore, the shift of Curie temperature to higher temperatures was attributed to internal stress resulting from the formation of a core–shell structure and a large amount of secondary phase grains.

Effects of Nb/Co Ratio on the Dielectric Properties of BaTiO3-based X7R Ceramics

Effects of Rare Earth Elements on the Dielectric Properties of BaTiO<sub>3</sub>-Based X7R Materials

Effects Of Rare Earth Elements On The Dielectric Properties Of Batio3-Based X7r Materials

The role of Co in the BaTiO3–Na0.5Bi0.5TiO3 based X9R ceramics

Dielectric behaviors of Nb2O5–Co2O3 doped BaTiO3–Bi(Mg1/2Ti1/2)O3 ceramics

Colossal Dielectric Permittivity in (al+nb) Co-Doped Ba0.4Sr0.6TiO3 Ceramics

The effect of doping process on microstructure and dielectric properties of BaTiO 3 -based X7R materials

Doping Behaviors of Nb2O5 and Co2O3 in Temperature Stable BaTiO3-based Ceramics

The effect of doping process on microstructure and dielectric properties of BaTiO3-based X7R materials

Effects of BiNbO<sub>4</sub> on the microstructure and dielectric properties of BaTiO<sub>3</sub>-based ceramics

Effect of Na0.5Bi0.5TiO3 on Dielectric Properties of BaTiO3 Based Ceramics

Effect of Sr/Ba Ratio on Dielectric Properties of BSTN Ceramics

Microstructures and Microwave Dielectric Properties of Ba((Co0.55Zn0.35Mg0.1)1/3Nb2/3)O3‐BaZrO3 Ceramics

Effects of BiNbO 4 on the microstructure and dielectric properties of BaTiO 3 -based ceramics

Effects of Nb 2 O 5 Doping on the Microstructure and the Dielectric Temperature Characteristics of Barium Titanate Ceramics

Effects of Sintering Temperature on the Dielectric Properties of Batio3 Based X7r Ceramics

Investigation on dielectric properties of BaTiO3 co-doped with Ni and Nb

Effects of Ta2o5/Y2o3 Codoping on the Microstructure and Microwave Dielectric Properties of Ba(Co0.56zn0.40)(1/3)Nb2/3o3 Ceramics

Effects of Sintering Temperature and Bi2O3, Y2O3 and MgO Co-Doping on the Dielectric Properties of X8R BaTiO3-based Ceramics

The Effects of Gd/Nd Co-Doping on the Microstructure and Dielectric Properties of Batio3 Ceramics

Effects of W,Ti Co-Doping on the Microstructure and Microwave Dielectric Properties of Ba5nb4o15 Ceramics