Effects of Phase Constitution and Microstructure on Energy Storage Properties of Barium Strontium Titanate Ceramics
Yong Jun Wu,Yu Hui Huang,Nan Wang,Juan Li,Mao Seng Fu,Xiang Ming Chen
DOI: https://doi.org/10.1016/j.jeurceramsoc.2016.12.052
IF: 5.7
2017-01-01
Journal of the European Ceramic Society
Abstract:Barium strontium titanate (Ba0.3Sr0.7TiO3, BST) ceramics have been prepared by conventional sintering (CS) and spark plasma sintering (SPS). The effects of phase constitution and microstructure on dielectric properties, electrical breakdown process and energy storage properties of the BST ceramics were investigated. The X-ray diffraction analysis and dielectric properties measurements showed that the cubic and tetragonal phase coexisted in the SPS sample while the CS sample contained only tetragonal phase. Much smaller grain size, lower porosity, fewer defects and dislocation were observed in SPS samples, which greatly improved the electrical breakdown strength of the Ba0.3Sr0.7TiO3 ceramics. The enhanced breakdown strength of the SPS samples resulted in an improved maximum electrical energy storage density of 1.13J/cm3 which was twice as large as that of the CS sample (0.57J/cm3). Meanwhile, the energy storage efficiency was improved from 69.3% to 86.8% by using spark plasma sintering.