Dielectric and energy storage properties of ternary doped barium titanate-based ceramics
Hailin Zhang,Youya Ke,Haochen Duan,Lian Deng,Huanfu Zhou,Xiuli Chen
DOI: https://doi.org/10.1007/s10854-024-13928-z
2024-12-06
Journal of Materials Science Materials in Electronics
Abstract:In this study, lead-free ceramics (1− x )[0.90BaTiO 3 –0.10Bi(Mg 1/2 Ti 1/2 )O 3 ]– x (Na 0.5 Bi 0.5 ) 0.7 Sr 0.3 TiO 3 (abbreviated as (1− x )(BT-BMT)– x BNST, x = 0.00, 0.05, 0.10, 0.15, and 0.20) were prepared using the solid-phase reaction method. The effect of (Na 0.5 Bi 0.5 ) 0.7 Sr 0.3 TiO 3 (BNST) doping on the dielectric and energy-storage properties of 0.90BaTiO 3 –0.10Bi(Mg 1/2 Ti 1/2 )O 3 (BT-BMT) ceramics was investigated. The maximum polarization strength ( P max ) was obtained when x = 0.15 at a breakdown field ( E b ) of 480 kV/cm, and the optimal energy-storage performance was W rec = 4.25 J/cm 3 and η = 87.49%. Excellent stability in both frequency and temperature was observed in the frequency conversion range of 1–120 Hz and variable temperature test from 30 to 140 °C. Moreover, the BT-BMT–0.15BNST energy-storage ceramics with rapid discharge ( t 0.9 = 4 ~ 47 ns), high power density ( P D = 155.2 MW/cm 3 ), and stable performance have great potential in pulse capacitors. In this study, we successfully developed ternary-doped energy-storage ceramics with outstanding energy-storage capabilities in BNT matrices. We comprehensively examined their crystal structures, microstates, and energy-storage properties. These insights offer new perspectives for research in the field of lead-free barium titanate-based ceramics.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied