Abstract:A comprehensive modeling framework for the thermoforming of polymer matrix woven laminate composite was developed. Two numerical indicators, the slip path length and traction magnitude, have been identified to be positively correlated to matrix smearing and wrinkling defects. The material model has been calibrated with picture-frame experimental results, and the prediction accuracy for intra-ply shear and thickness distribution was examined with measurements of the physically formed parts. Specifically, thickness prediction for most locations on the formed parts was accurate within an 11.6% error margin. However, at two points with significant intra-ply shear, the prediction errors increased to around 20%. Finally, a parametric study was conducted to determine the relationship between various process parameters and the quality of the formed part. For the trapezoidal part, orienting the laminate at 45 degrees to the mold axis reduces the likelihood of matrix smear and wrinkling defects. Although this laminate orientation yielded a greater spatial variation in part thickness, the thickness deviation is lower than that for the 0-degree orientation case. Two forming analyses were conducted with ramp rates of 25 mm/s and 80 mm/s to match the equipment's operational limits. It was observed that higher forming rates led to a greater likelihood of defects, as evidenced by a 15% and 10% increase in the formed part areas with longer slip paths and higher traction magnitudes, respectively. It was discovered that shallower molds benefit from faster ramp rates, while deeper molds require slower rates to manage extensive shearing, stretching and bending. Faster forming rates lead to smaller thickness increases at high intra-ply shear regions, indicating a shift from intra-ply shear to out-of-plane bending due to the visco-plastic effect of the molten laminate and can negatively impact part quality. Lastly, it was shown that a well-conceived strategy using darts could improve the part quality by reducing the magnitude of the defect indicators.

Characterization of Intra‐ply Shear Behaviors of Unidirectional Prepregs During Hot Diaphragm Forming Process

Analysis and Characterization of Interlaminar Tack for Different Prepreg Materials During Automated Fiber Placement

Inter-Ply Slipping Behaviors and Kinetic Equation of Carbon Fiber-Reinforced Epoxy Prepregs for Hot Diaphragm Preforming

Interply friction of carbon fiber/epoxy prepreg stacks under different processing conditions

Influence of Process Parameters on the Interlaminar Shear Strength of CF/PEEK Composites In-Situ Consolidated by Laser-Assisted Automated Fiber Placement

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

Efficient numerical analysis of in-plane compression-induced defects in thick multi-ply woven textile preforms during double diaphragm forming

YIELD POINT AND STRESS RELAXATION BEHAVIOR OF PLY-PLY INTERACTION OF THERMOSET PREPREGS

Modeling on the Effect of Automated Fiber Placement Induced Gaps in Curved Composite Laminates

Experimental characterisation and constitutive modelling of the intra-ply tensile and shear properties of unidirectional fibre reinforced thermoplastics (UD FRTPs) under solid-state stamp forming conditions

Experimental study on the mechanical behavior of laminates made by fiber steering: Influence of fiber angle and tow width

Characterizing the Stress Relaxation Behavior of Unidirectional Prepreg through a Parallel Fractional-Order Viscoelastic Model

Experimental and numerical investigations on thermoforming of thermoplastic prepregs of glass fiber reinforced nylon 6

A Modeling Framework for the Thermoforming of Carbon Fiber Reinforced Thermoplastic Composites

Characterization of tool-ply friction behavior for treated jute/PLA biocomposite prepregs in thermoforming

Double diaphragm forming simulation for complex composite structures

Influence of the Unit Cell Parameters on the Thermomechanical Non-Symmetric In-Plane Shear Behavior of 2D Biaxial Braided Preform for Thermoplastic Biocomposites

Characterisation of bending mechanics in uncured laminated materials using a modified Dynamic Mechanical Analysis

Compaction behavior of 3D woven preforms with hybrid fibers and under different process parameters

Effect of forming temperature and fiber orientation on the warm deep drawing formability of TA2/Cf/PEEK laminates

Experimental and numerical studies on two-point incremental forming of woven fabric composite sheet