Abstract:The glass fiber-reinforced metal laminates (GLARE) cannot be used to form complex laminate structures in the aerospace industry, because there is substantial variation in the plasticity of the heterogeneous materials. Hence, a compound process for composite materials based on the thermoforming technology for aluminum alloy and fiber-reinforced metal laminates (FMLs)-forming technology was proposed; it contains solution heat treatment, thermoforming, quick cold die quenching, artificial aging integrated process (HFQ), and the thermal consolidation of fiber-reinforced metal laminates, and it is named the HFQ-FMLs forming process. In order to test and judge the effect of the heat treatment on the properties of the materials obtained by the new technology, the pure metal sheet and the three kinds of HFQ-FMLs composite laminates fabricated with the different layup method were assessed with the Vickers hardness test and the Charpy impact test at the same time, and they were labeled #1, #2, #3, #4, respectively. In the Charpy impact test, in order to obtain accurate data, the shape and fixing position of the specimen was optimized so that the gap direction was parallel to the loading direction. After the heat treatment, the properties of the aluminum alloy were improved, the hardness will affect the energy absorption of the laminates, and the relationship between the thickness, hardness and impact properties will be analyzed. The hardness test results are 39.9 HV, 37.5 HV, 37.4 HV, 37.1 HV which indicates the pure metal sheet had the greatest hardness, and the greater the thickness of fiber layer, the lower was the hardness of the HFQ-FMLs composite laminate. The impact resistance of the HFQ-FMLs composite laminates was about two times of the pure metal sheet for the same thickness, and the values are 2.3 J, 4.8 J, 4.8 J, 4.8 J, respectively. In addition, the method of laying the fiber layer had no effect on the impact resistance of the composite laminates. For the novel composite laminates subjected to different cutting processes, the scanning electron microscope (SEM) results for the incision morphology suggest that the water cutting process ensures the structural integrity of the composite laminates after the edges' and holes' cutting procedures, and the performance maintains continuity.

Effect of forming temperature and fiber orientation on the warm deep drawing formability of TA2/Cf/PEEK laminates

Investigation into the Fiber Orientation Effect on the Formability of GLARE Materials in the Stamp Forming Process

Interlayer Friction Mechanism and Scale Effects in Ultra-Thin TA1 Titanium Alloy/Carbon Fiber-Reinforced Plastic Laminates

Ultrasonic-assisted preparation-forming-curing process for ultra-thin micro-fiber metal laminates: Deformation characteristics

An Investigation into the Forming of Fiber Metal Laminates with Different Thickness Metal Skins Using Hydromechanical Deep Drawing

An Experimental and Simulation Study on the Formability of Commercial Pure Titanium Foil

Atomistic Modeling of the Effect of Temperature on Interfacial Properties of 3D-Printed Continuous Carbon Fiber-Reinforced Polyamide 6 Composite: From Processing to Loading

Deep drawing of fiber metal laminates using an innovative material design and manufacturing process

Characterization and Formability of Titanium/Aluminum Laminate Composites Fabricated by Hot Pressing

Structure Design on Thermoplastic Composites Considering Forming Effects

Extraordinary room temperature tensile ductility of laminated Ti/Al composite: Roles of anisotropy and strain rate sensitivity

Numerical and experimental investigations on the effects of variable cavity pressure on the formability of GLARE using hydromechanical deep drawing

Experimental Research on the Thermal-Consolidation Compound Forming of Thermosetting Fiber Metal Laminates Design for Complex Structures with Variable Curvature

The Synergistic Effect of Temperature and Loading Rate on Deformation for Thermoplastic Fiber Metal Laminates

Effects of Thermoforming Parameters on Woven Carbon Fiber Thermoplastic Composites

Effects of temperature and fiber orientation on the tensile behavior of short carbon fiber reinforced PEEK composites

Process parameter–mechanical property relationships and influence mechanism of advanced CFF/PEEK thermoplastic composites

The Optimization of Process Parameters and Characterization of High-Performance CF/PEEK Composites Prepared by Flexible CF/PEEK Plain Weave Fabrics

The effects of processing parameters on the wedge peel strength of CF/PEEK laminates manufactured using a laser tape placement process

Influence of lay‐up sequences on cylindrical parts drawability of CFRP laminates

Open-hole Tensile Progressive Damage and Failure Prediction of Carbon Fiber-Reinforced PEEK–titanium Laminates