Abstract:The glass fiber-reinforced metal laminates (GLARE) cannot be used to form complex laminate structures in the aerospace industry, because there is substantial variation in the plasticity of the heterogeneous materials. Hence, a compound process for composite materials based on the thermoforming technology for aluminum alloy and fiber-reinforced metal laminates (FMLs)-forming technology was proposed; it contains solution heat treatment, thermoforming, quick cold die quenching, artificial aging integrated process (HFQ), and the thermal consolidation of fiber-reinforced metal laminates, and it is named the HFQ-FMLs forming process. In order to test and judge the effect of the heat treatment on the properties of the materials obtained by the new technology, the pure metal sheet and the three kinds of HFQ-FMLs composite laminates fabricated with the different layup method were assessed with the Vickers hardness test and the Charpy impact test at the same time, and they were labeled #1, #2, #3, #4, respectively. In the Charpy impact test, in order to obtain accurate data, the shape and fixing position of the specimen was optimized so that the gap direction was parallel to the loading direction. After the heat treatment, the properties of the aluminum alloy were improved, the hardness will affect the energy absorption of the laminates, and the relationship between the thickness, hardness and impact properties will be analyzed. The hardness test results are 39.9 HV, 37.5 HV, 37.4 HV, 37.1 HV which indicates the pure metal sheet had the greatest hardness, and the greater the thickness of fiber layer, the lower was the hardness of the HFQ-FMLs composite laminate. The impact resistance of the HFQ-FMLs composite laminates was about two times of the pure metal sheet for the same thickness, and the values are 2.3 J, 4.8 J, 4.8 J, 4.8 J, respectively. In addition, the method of laying the fiber layer had no effect on the impact resistance of the composite laminates. For the novel composite laminates subjected to different cutting processes, the scanning electron microscope (SEM) results for the incision morphology suggest that the water cutting process ensures the structural integrity of the composite laminates after the edges' and holes' cutting procedures, and the performance maintains continuity.

An Investigation into the Forming of Fiber Metal Laminates with Different Thickness Metal Skins Using Hydromechanical Deep Drawing

Numerical and experimental investigations on the effects of variable cavity pressure on the formability of GLARE using hydromechanical deep drawing

Investigation into the Fiber Orientation Effect on the Formability of GLARE Materials in the Stamp Forming Process

Deep drawing of fiber metal laminates using an innovative material design and manufacturing process

Experimental Research on the Thermal-Consolidation Compound Forming of Thermosetting Fiber Metal Laminates Design for Complex Structures with Variable Curvature

Mechanical properties and formability behavior of glass-reinforced aluminum laminate, developed by semi-cured process

A novel active hydroforming & curing process to manufacture GLARE laminates: Numerical and experimental investigations

A state-of-the-art review on mechanical characteristics of different fiber metal laminates for aerospace and structural applications

Forming challenges of small and complex fiber metal laminate parts in aerospace applications—a review

Experimental study for the effect of hole notched in fracture mechanics of GLARE and GFRP composites subjected to quasi-static loading

Investigation of Forming Behaviour of Metal-Polymer Sandwich Composite through Limit Dome Height Test Simulations

Effect of forming temperature and fiber orientation on the warm deep drawing formability of TA2/Cf/PEEK laminates

Fiber Metal Laminates Based on Natural/Synthesis Fiber Composite for Vehicles Industry: an Experimental Comparative Study

Experimental failure analysis and mechanical performance evaluation of fiber-metal sandwich laminates interleaved with polyamide-6,6 interlayers through the combined usage of acoustic emission, thermography and microscopy techniques

Investigation on the multiple plies structure of aluminum-lithium alloy and glass fiber composite with respect to deformation failure

Mechanical and microstructural characterization of hybrid fiber metal laminates obtained through sustainable manufacturing

Ultrasonic-assisted preparation-forming-curing process for ultra-thin micro-fiber metal laminates: Deformation characteristics

Synergistic Mechanism of Strengthening and Toughening of Tissue Regulation Response to Mg/Al Composite Laminates by Hard Plate Accumulative Roll Bonding

Investigation of structure–flexural response relations in thermoplastic carbon/glass fiber‐metal laminates

GLARE deformation in low-restraint state: Tensile and bending behavior

Evaluation of tensile properties of fiber metal laminates under different strain rates