Performance improvement of DBP-based solar cells by introducing a luminescent sensitizer bis[(4,6-difluorophenyl)-pyridinato-N,C 2′ ]c(picolinate)iridium(III) (FIrpic)

Jie Tang,Weiguang Li,Juncong Chen,Yanqiong Zheng,Junbiao Peng,Jianhua Zhang,Bin Wei,Xifeng Li

DOI: https://doi.org/10.1007/s11706-021-0533-0

2021-01-01

Frontiers of Materials Science

Abstract:In this work, a sky-blue luminescent down-shifting (LDS) layer bis[(4,6-difluorophenyl)-pyridinato-N,C 2′ ]c(picolinate)iridium(III) (FIrpic) was inserted between tetraphenyldibenzoperiflanthene (DBP) and MoO 3 as UV-screen and sensitizer for small molecule DBP/C 60 based planar heterojunction (PHJ) solar cells. With 8-nm FIrpic the short circuit current ( J sc ) and power conversion efficiency (PCE) of the device are enhanced by 28% and 15%, respectively, probably originating from the re-absorption of the photons emitted from FIrpic. The V oc linearly increases over 1-nm FIrpic, ascribed to the deeper HOMO level of FIrpic than DBP, while the fill factor continuously declines from 3- to 10-nm FIrpic. The EQE spectra prove that the J sc is mainly contributed by the photocurrent generated in DBP and C 60 layers. When the FIrpic thickness is 8 nm, the film surface is very uniform with the smallest water contact angle. The impedance spectroscopy demonstrates that the device resistance gradually increases from 4.1×10 4 Ω (without FIrpic) to 4.6×10 4 Ω (with 10-nm FIrpic) with the FIrpic thickness rise, simultaneously the device transits from the insulating state into the conductive state faster for the thin FIrpic layer than the thick layer.