Mid-Permittivity Microwave Dielectric Ceramics Based On Catio3-Realo3 (Re=La, Nd, Sm) Perovskite Solid Solutions

B Jancar,D Suvorov,M Valant

2003-01-01

Abstract:Based on the CaTiO3 REAlO3 (RE = La, Nd, Sm) solid-solution systems we synthesized microwave dielectric ceramics with temperature-stable resonant frequencies (tau(f) approximate to 0 ppnL/K), that exhibit epsilon(r) > 40 and Qxf > 40000 GHz. A more detailed study of the CaTiO3-NdAlO3-based ceramics revealed that the Q-value can be strongly influenced by the processing parameters. Using SEM and TEM analyses we found that during the solid-state reaction hexaluminate inclusions form as a transient phase. Their concentration in the microstructure of sintered ceramics depends on the thoroughness of the calcination process. In order to decrease the extrinsic dielectric losses (increase the Q-value) the amount of hexaluminate inclusions needs to be minimized. Apart from these inclusions the Q-value of the CaTiO3-NdAlO3 ceramics is influenced by the cooling rate after sintering. Slower cooling results in higher Q-value. When subjected to a thorough calcination (1300degreesC/30 hours with intermediate homogenization) and slow cooling after sintering (< 0.5 K/min), the 0.7CaTiO(3)-0.3NdAlO(3) ceramics exhibit tau(f) approximate to 0 ppm/K, epsilon(r) = 44 and Qxf = 44000 GHz.