Abstract:CaNdAlO4 microwave dielectric ceramics were modified by Ca/Ti co-substitution, and their dielectric characteristics were evaluated along with their structure and microstructures. Ca1+xNd1-xAl1-xTixO4 (x=0, 0.025, 0.05, 0.10, 0.15, 0.20) ceramics with the relative density of over 95% theoretical density were obtained by sintering at 1400 degrees-1450 degrees C in air for 3 h, where the K2NiF4-type solid solution single phase was determined from the compositions of x<0.20, while a small amount of CaTiO3 secondary phase was detected for x=0.20. With Ca/Ti co-substitution in CaNdAlO4 ceramics, the dielectric constant (epsilon(r)) increased with increasing x, and the temperature coefficient of resonant frequency (tau(f)) was adjusted from negative to positive, while the Q x f(0) value increased significantly at first and reached an extreme value at x=0.025 and the maximum at x=0.15. The best combination of microwave dielectric characteristics were achieved at x=0.15 (epsilon(r)=19.5, Q x f(0)=93 400 GHz, tau(f) = -2 ppm/degrees C). The improvement of the Q x f(0) value primarily originated from the reduced interlayer polarization with Ca/Ti co-substitution, while the decreased tolerance factor, the subsequent increased interlayer stress, and the appearance of CaTiO3 secondary phase brought negative effects upon the Q x f(0) value.

Phase Structures and Microwave Dielectric Properties of Xcatio3–(1 − X)sm0.9nd0.1alo3 Ceramics

Microwave Dielectric Properties of Temperature Stable (1-X)srlaalo4-xtio2 Composite Ceramics

Crystal Structure, Vibrational Spectroscopy, and Microwave Dielectric Properties of CaAl4O7 Ceramics with Low Permittivity

Crystal Structure, Infrared Reflectivity Spectra and Microwave Dielectric Properties of CaAl2O4 Ceramics with Low Permittivity

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Characterization and Microwave Dielectric Properties of TiO2-modified 0.65catio3–0.35sm0.9nd0.1alo3 Ceramics

Structure evolution and improved microwave dielectric characteristics in CaTi1-x(Al0.5Nb0.5)xO3 ceramics

Structure and microwave dielectric characteristics of (Sr1−xCax)Nd2Al2O7 ceramics

Millimeter‐wave dielectric characteristics of Sr1−xCaxSmAlO4 ceramics

A novel low-loss (1-x)(Ca0.8Sr0.2)TiO3-xSmAlO3 microwave dielectric ceramics with near-zero temperature coefficient

Structure and Microwave Dielectric Characteristics of Ca1+xNd1−xAl1−xTixO4 Ceramics

Structure Evolution and Microwave Dielectric Characteristics of Ca[(Alxga0.5-Xnb0.5)(0.5)Ti-0.5]O-3 Ceramics

Structure and microwave dielectric characteristics of Ca1-xNd2x/3TiO3 ceramics

Structure And Microwave Dielectric Characteristics Of Ca1+Xnd1-Xal1-Xtixo4 Ceramics

Structure and Microwave Dielectric Properties of SrLa[Al1−x(Mg0.5Ti0.5)x]O4 (x = 0.2–0.8) Ceramics

Microstructures and Microwave Dielectric Properties of the CaSmAlO4‐Based Ceramics

Microstructures and Microwave Dielectric Properties of the CaSmAlO<sub>4</sub>-Based Ceramics

Impedance spectroscopy, B-site cation ordering and structure–property relations of (1 − x) La[Al0.9(Mg0.5Ti0.5)0.1]O3–x CaTiO3 ceramics for 5G dielectric waveguide filters

Structural Phase Transition and Microwave Dielectric Properties of Ca1−x Sr X TiO3 (x = 0.1–0.9) Ceramics

Nonstoichiometric microwave dielectric ceramics [(Na0.5-xBi0.5+x/3)0.5Ca0.5]MoO4 with low sintering temperatures