Enhanced electrochemical performance of La-doped Li-rich layered cathode material
Meng Wang,Lin Chen,Meng Liu,Yunbo Chen,Yijie Gu
DOI: https://doi.org/10.1016/j.jallcom.2020.156620
IF: 6.2
2020-12-01
Journal of Alloys and Compounds
Abstract:<p>A series of promising lithium-rich cathode materials with excellent electrochemical properties were successfully synthesized by calcining precursors and lithium salts. The structure, morphology, element valence state, cyclic voltammetry and electrochemical impedance were used to study the properties of the materials. The doped La<sup>3+</sup> had great influence on the structure and electrochemical properties of the materials. XRD results displayed that La<sup>3+</sup> was incorporated into the material lattice resulted in the formation of layered-spinel hetero-structure, the decrease of cation mixing and the expansion of <em>c</em> lattice parameter. The discharge capacity decreased after La<sup>3+</sup> was doped into Li[Li<sub>0.2</sub>Mn<sub>0.54</sub>Ni<sub>0.13</sub>Co<sub>0.13</sub>]O<sub>2</sub>, which was due to La<sup>3+</sup> was non-electrochemical active element did not participate in the electrical reaction. Although the discharge capacity was reduced after La<sup>3+</sup> doping, the initial coulombic efficiency, cycling performance and rate capability were all improved. Among the prepared samples, Li[Li<sub>0.2</sub>Mn<sub>0.54</sub>Ni<sub>0.13</sub>Co<sub>0.125</sub>]La<sub>0.005</sub>O<sub>2</sub> delivered the best electrochemical performance and highest lithium ions diffusion coefficient, which can be ascribed to its stable and ordered layered-spinel hetero-structure.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering