Performance of Li[Li0.2Mn0.54Co0.13Ni0.13] O2 Coated with Α-Lialo2

CHEN Yu,PANG Guo-yao,LI Jian-ling

DOI: https://doi.org/10.3969/j.issn.1001-1579.2012.05.002

2012-01-01

Abstract:Co-precipitation method was used to synthesize the solid solution cathode material Li[Li0.2Mn0.54Co0.13Ni0.13]O2 and the performance of this material coated with lithium aluminate(α-LiAlO2) was studied.XRD and field-emission scanning electron microscopy(FESEM) test showed that both the materials before and after coating belonged to α-NaFeO2 hexagonal layered structure with R3m space group,the thick inhomogeneous floccus layers were coated on the surface of particle.The better performance was achieved by sample with coating amount of 3%:when cycled in 2.0～4.8 V at a low current (0.05 C),the specific discharge capacity was 273.0 mAh/g,when the current increased to 1.00 C,the specific discharge capacity reached to 173.2 mAh/g.The rate capability was benefitted from the lower surface impedance and reaction impedance as indicated by the electrochemical impedance spectroscopy(EIS) test result.