Abstract:CaMg 2 Bi 2 -based compounds, a kind of the representative compounds of Zintl phases, have uniquely inherent layered structure and hence are considered to be potential thermoelectric materials. Generally, alloying is a traditional and effective way to reduce the lattice thermal conductivity through the mass and strain field fluctuation between host and guest atoms. The cation sites have very few contributions to the band structure around the fermi level; thus, cation substitution may have negligible influence on the electric transport properties. What is more, widespread application of thermoelectric materials not only desires high Z T value but also calls for low-cost and environmentally benign constituent elements. Here, Ba substitution on cation site achieves a sharp reduction in lattice thermal conductivity through enhanced point defects scattering without the obvious sacrifice of high carrier mobility, and thus improves thermoelectric properties. Then, by combining further enhanced phonon scattering caused by isoelectronic substitution of Zn on the Mg site, an extraordinarily low lattice thermal conductivity of 0.51 W m -1 K -1 at 873 K is achieved in (Ca 0.75 Ba 0.25 ) 0.995 Na 0.005 Mg 1.95 Zn 0.05 Bi 1.98 alloy, approaching the amorphous limit. Such maintenance of high mobility and realization of ultralow lattice thermal conductivity synergistically result in broadly improvement of the quality factor β . Finally, a maximum Z T of 1.25 at 873 K and the corresponding Z T a v e up to 0.85 from 300 K to 873 K have been obtained for the same composition, meanwhile possessing temperature independent compatibility factor. To our knowledge, the current Z T a v e exceeds all the reported values in AMg 2 Bi 2 -based compounds so far. Furthermore, the low-cost and environment-friendly characteristic plus excellent thermoelectric performance also make the present Zintl phase CaMg 2 Bi 2 more competitive in practical application.

Zintl Phase Yb1–xBaxMg2Bi1.98 Compounds with Enhanced Thermoelectric Performance Caused by Cation Substitution

Zintl Phase Yb 1– x Ba x Mg 2 Bi 1.98 Compounds with Enhanced Thermoelectric Performance Caused by Cation Substitution

Thermoelectric Properties of Zn-Doped YbMg1.85−xZnxBi1.98

Achieving High Thermoelectric Performance in Rare-Earth Element-Free CaMg 2 Bi 2 with High Carrier Mobility and Ultralow Lattice Thermal Conductivity

Enhanced Thermoelectric Performance in SmMg 2 Bi 2 via Ca-Alloying and Ge-Doping

Improved Thermoelectric Performance in the Zintl Phase Compounds YbZn2−xMnxSb2 Via Isoelectronic Substitution in the Anionic Framework

Thermoelectric transport properties of CaMg2Bi2, EuMg2Bi2, and YbMg2Bi2

High Thermoelectric Performance of CaMg 2 Bi 2 Enabled by Dynamic Doping and Orbital Alignment

Enhanced thermoelectric performance of P-type CaMg2Bi1.98 and optimized CaAl2Si2-type Zintl phase module with equal cross-section area

New Zintl Phase Yb10MgSb9 with High Thermoelectric Performance

Balancing the anionic framework polarity for enhanced thermoelectric performance in YbMg2Sb2 Zintl compounds

A14MgBi11 (A = Ca, Sr, Eu): Magnesium Bismuth Based Zintl Phases As Potential Thermoelectric Materials

Thermoelectric Properties of Zintl Compound Ybzn2sb2 with Mn Substitution in Anionic Framework

High performance of Mg3Bi1.5Sb0.5 based materials for power generation: Revealing the counter-intuitive effect of tuning Bi content on the thermoelectric properties

High‐Performance CaMg2Bi2‐Based Thermoelectric Materials Driven by Lattice Softening and Orbital Alignment via Cadmium Doping

Planar Zintl-phase high-temperature thermoelectric materials XCuSb (X = Ca, Sr, Ba) with low lattice thermal conductivity

Mechanism of Thermoelectric Performance Enhancement in CaMg2Bi2‐Based Materials with Different Cation Site Doping

Improved figure of merit (z) at low temperatures for superior thermoelectric cooling in Mg3(Bi,Sb)2

Na/Bi-co-doping and Heterogeneous Interfaces Leading to Enhanced Thermoelectric Performance of P-Type Mg3Sb2-based Zintls

High-Performance Mg<sub>3</sub>Sb<sub>2-<i>x</i></sub>Bi<i><sub>x</sub></i> Thermoelectrics: Progress and Perspective

Enhancing thermoelectric performance of AB 2 Sb 2 -type Zintl phase through band shaping and lattice distortion