Abstract:The present paper focuses on the heat transfer and contact pressure at the casting-die interface in squeeze casting process. Experiments were conducted and a "plate shape" was used to cast aluminum alloy A356 in H13 steel die. Based on the temperature measurements inside the die, the interfacial heat transfer coefficient (IHTC) at the metal-die interface was determined by applying an inverse approach. The pressure at the metal-die interface was measured by using Kistler pressure transducer. The acquired data were processed by a low pass filtering method based on Fast Fourier Transform (FFT). Besides, a set of methods was set up to verify the computer program for the inverse model. The results show that the pressure at the casting-die interface and the IHTC rose to the peak value almost simultaneously as soon as the pressure was applied by the press. The higher the applied pressure, the higher the peak value of the IHTC and the pressure at the casting-die interface. It was a pressure maintaining stage immediately after the pressure was applied. During this stage, the pressure at the casting-die interface decreased immediately after it reached the peak value. The IHTC sharply dropped at the beginning. Then, the decrease rate of the IHTC became lower and lower. Besides, the IHTC of the cases with pressure applied was much higher than those without pressure applied. It indicates that the applied pressure greatly improved the contact status of casting and die surfaces and reduced the thermal resistance between the two surfaces. The IHTC profiles of the cases with the pressures 23 MPa and 46 MPa applied did not make much difference, however, when the applied pressure reached 70 MPa, the influence of the pressure at the casting die interface on the IHTC became very remarkable. (C) 2017 Elsevier Ltd. All rights reserved.

High Pressure Counter-Pressure Casting Process And Its Control System

Optimization of Valve Body Process Based on HZCAE

Process Optimization of Low-pressure Die Casting of Aluminum Alloy Wheel based on Taguchi Method

Prediction method of shrinkage cavity and shrinkage porosity in solidification process under low-pressure casting

Finite element analysis for die casting parameters in high-pressure die casting process

Study on Casting Defect Control of Austenitic 304 Complex Structural Parts

Accurate Simulation of Complex Temperature Field in Counter-Pressure Casting Process Using A356 Aluminum Alloy

Mechanism and Application of A Newly Developed Pressure Casting Process: Horizontal Squeeze Casting

Integrated optimization system for high pressure die casting processes

Study on Numerical Simulation of Mold Filling and Solidification Processes under Pressure Conditions

Solidification simulation of automobile wheel in low pressure casting

Experimental Study on the Heat Transfer Behavior and Contact Pressure at the Casting-Mold Interface in Squeeze Casting of Aluminum Alloy

Innovative Hybrid High-Pressure Die-Casting Process for Load-Bearing Body-In-White Structural Components

Optimization of the Synchronous Pressurization Process for the Elimination of Double-Layer Oxide Film Defects

Quality Control Study on High Pressure Casting Based on Magma and Ultra-red Simulation

A novel nonlinear pressurization method for counter-gravity casting of cross-sectional mutation structures

Low pressure casting technology and forming process analysis of metal mold based on ProCAST FEA procedure

Effect of different processing parameters on interfacial heat-transfer behavior in high-pressure die-casting process

Effects of Process Parameters on Internal Quality of Castings During Novel Casting

Digital Foundry Technology For Automobile Hot Stamping Die

Progress in numerical simulation of casting process