Glass Bonded Nd-Fe-B Magnets

Jm Yao,Mf Hsieh,Ts Chin,Sk Chen

1996-01-01

Abstract:Resin bonded SmCo5 and N(d)2Fe(14)B magnets have wide industrial applications. They are usually soft and can't withstand heat and moisture. In this study, improvement in hardness and moisture resistance of bonded magnets are explored by using, as the bonding agent, low-melting Sn-Pb-P-O-Cl glasses (SnCl2 45mol%, P2O5 40mol%, and PbCl2 15mol%) with glass transition and softening temperatures of 197 degrees C and 225 degrees C, respectively. The glass is transparent and water resistant (the dissolution rate at 33 degrees C water is 1.14x10(-7) g/cm(2).min) with a density of 3.91 g/cm(3). Melt-spun NdFeB (MQI) flakes were ground and mixed with the glass frit with weight percentage of glass at 15%, 20%, or 25%. They were then hot pressed (300 similar to 500 degrees C for 10 min, 124 MPa) in air or under vacuum of 2x10(-4) Pa. Typical magnetic properties of 400 degrees C similar to 500 degrees Cx10 min hot-pressed magnets (20wt.% glass) are Br: 4.8 similar to 5.0 kG, iHc: 13.1 similar to 14.3 kOe, bHc: 4.3 kOe, (BH)m 5.2 similar to 5.5 MGOe with a density of 5.43 similar to 5.92 g/cc. The hardness of the magnets can be as high as HV 230 similar to 330. Hot pressed MQI powder compacts without glass at 700 degrees Cx10 min was prepared for comparison. Microstructure and the effect of processing on magnetic properties of the magnets are presented.