Roles of Y and Fe contents on glass-forming ability, thermal stability, and magnetic properties of Co-based Co–Fe–Y–B bulk metallic glasses

Xinyu Liang,Yanhui Li,Feng Bao,Zhengwang Zhu,Haifeng Zhang,Wei Zhang

DOI: https://doi.org/10.1016/j.intermet.2021.107135

IF: 4.075

2021-05-01

Intermetallics

Abstract:<p>Soft magnetic Co-based bulk metallic glasses (BMGs) with large supercooled liquid region (Δ<em>T</em>_x) and high saturation magnetic flux density (<em>B</em>_s) have been developed in a new Co–Fe–Y–B alloy system. Addition of appropriate contents of Y and Fe into a Co₇₅B₂₅ alloy enlarges the Δ<em>T</em>_x and improves the glass-forming ability (GFA). Δ<em>T</em>_x of 50–64 K and a critical diameter of up to 2.0 mm have been achieved for the (Co_0.5–0.7Fe_0.3–0.5)_71.5Y_3.5B₂₅ BMGs. The coercivity (<em>H</em>_c) of Co_75-xY_xB₂₅ and (Co_0.7Fe_0.3)_75-xY_xB₂₅ (x = 0–5) alloy series shows a similar V-shape change with Y content, and gets the minimum at x = 3.5, while that of (Co_1-yFe_y)_71.5Y_3.5B₂₅ (y = 0–0.5) alloys keeps rising with the increase of Fe content. The <em>B</em>_s of the alloys monotonically decreases with more Y addition and increases with enriching of Fe. The (Co_0.5–0.7Fe_0.3–0.5)_71.5Y_3.5B₂₅ BMGs exhibit high <em>B</em>_s of 1.00–1.17 T and low <em>H</em>_c of 5.4–6.4 A/m. The BMGs possess high yield strength of 3978–4152 MPa with distinct plastic strain of up to 0.9% and Vickers hardness of 1218–1233 as well. The possible mechanisms of Y and Fe affecting the GFA, thermal stability, and magnetic properties of the Co-based Co–Fe–Y–B metallic glasses have been discussed.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering