Effects of C/B ratio on glass-forming ability and low-temperature magnetic behavior of FeCoCrMoCBTm metallic glass

Qianqian Wang,Xian Yang,Zhiqiang Cui,Lin Xue,Liliang Shao,Qiang Luo,Baolong Shen
DOI: https://doi.org/10.1016/j.jallcom.2020.158211
IF: 6.2
2021-05-01
Journal of Alloys and Compounds
Abstract:The effects of C/B ratio on the glass-forming ability (GFA) and low-temperature magnetic properties of Fe42Co6Cr15Mo14CxB21−xTm2 (x = 9, 11, 13, 15 and 17 at%) metallic glasses are studied in this work. The critical diameter of the bulk metallic glasses changes from 2 mm to 12 mm when x increases from 9 to 15, due to the dense atomic packing and strong liquid behavior. An Fe42Co6Cr15Mo14C15B6Tm2 amorphous master ingot with a diameter of 16.5 mm is produced via arc melting and furnace cooling. With increasing C/B ratio, the antiferromagnetic interactions between Fe and Cr is decreased, leading to the increasing Curie temperature and activation energy of spin-glass behavior. A stable magnetocaloric transition at a large temperature range is achieved in Fe42Co6Cr15Mo14C15B6Tm2 glassy ribbon. The fracture strength of the as-cast bulk metallic glasses increases firstly and then decreases with increasing C/B ratio, reaching the highest fracture strength of 4594 MPa when x = 15.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
Based on the provided literature information, this paper mainly explores the influence of the carbon - to - boron ratio (C/B ratio) on the glass - forming ability and low - temperature magnetic behavior of FeCoCrMoCBTm metallic glasses. Specifically, the researchers adjusted the proportion of carbon and boron in the alloy to observe how these changes affect the amorphous - forming ability of the material and its magnetic properties under low - temperature conditions. This research is of great significance for understanding the relationship between the microstructure and properties of metallic glasses and may provide theoretical guidance for the development of new high - performance metallic glass materials.