Study On The Behavior Of Elastic-Plastic Fracture Under Mixed I Plus Ii Mode Loading In Aluminum Alloy Ly12-J-Integral Analysis

Jb Sha,J Sun,P Zhu,Zj Deng,Hj Zhou

IF: 2.635

2000-01-01

International Journal of Fracture

Abstract:The elastic-plastic fracture behavior of aluminum alloy Ly12 under mixed I+II mode loading was studied by finite element method and fracture test. A mixed mode elastic-plastic fracture criterion of J-integral was proposed by using the J-resistance curve, and the maximum fracture effective plastic strain epsilon(p max) of different mixed ratios at crack tip were also calculated. The results show that,(1) the initiation J-integral values of different mixed ratios have the equation[GRAPHICS]where J(li) and J(IIi) are the mode I and mode II components of the mixed initiation J-integral J(MC) at a constant mixed ratio, respectively:(2) the relation between the J(MC) and mixed ratio K-I/K-II isJ(MC) = K-I(2) J(IC)/(K-I(2) + alpha K-II(2)) + alpha K-II(2)) + alpha K-II(2)) + alpha K-II(2) J(IIC)/(K-I(2) + alpha K-II(2)),where alpha = J(IC)/J(IIC);(3) J(MC) increases with an increasing of mode II component, J(IIC) is twice of J(IC) for Ly12; and(4) the maximum fracture effective plastic strain epsilon(p) max and stress triaxality sigma(m)/sigma of different mixed ratios at crack tip satisfy the formula ofepsilon(p) (max) exp(3 sigma(m)/2 sigma) = constant,where the constant is about 9.52 for Ly12. The relation with double parameters, epsilon(p) (max) and sigma(m)/sigma, can be used as the local fracture or damage mechanics parameter under mixed mode I+II loading.