Abstract:<p>The influence of microstructure (bimodal and lamellar structure) on the fatigue crack growth (FCG) rate of Ti–6Al–3Nb–2Zr–1Mo alloy was investigated using compact-tension (CT) specimens. The da/dN curves showed that the FCG rate of lamellar structure was slower than that of bimodal structure, especially in the early stage of crack growth. The FCG paths in the early stage were observed by optical microscopy and scan electric microscopy. The results revealed that the FCG paths of lamellar structure were more tortuous than that of bimodal structure. The frequency of crack deflection and bifurcation of the lamellar structure is significantly higher than that of bimodal structure. The dominant mode of crack propagation for bimodal structure is crossing βtrans and αp, and for lamellar structure is crossing α colonies. Fatigue crack growth mechanisms at the early stage have been studied by observation of crystalline orientation near the crack propagation path at the crack tip, in combination with the slip trace analyzing. The results show that the fatigue crack growth directions in αp or βtrans for bimodal structure and α colony for lamellar structure are mostly consistent with that of prismatic or basal plane trace. This indicated that the cracks propagation modes of crossing αp or βtrans in bimodal structure and crossing α colonies in lamellar structure are resulting from the slip band cracking of the microstructure at crack tip, as the evidence of <span class="math"><math>{101‾0}112‾0</math></span> prismatic dislocation lines were observed in αp or βtrans for bimodal structure and α colony for lamellar structure by transmission electron microscope (TEM) near the fracture surface.</p>

Numerical investigation of mechanical behavior of crack tip under mode I and mixed-mode I-II fatigue loading at negative load ratios

Experimental and numerical investigation on fatigue crack growth behavior of commercial pure titanium under I-II mixed mode loading at negative load ratios

Instrumented indentation measurements of residual stresses around a crack tip under single tensile overloads

Effects of Tensile/compressive Overloads on Fatigue Crack Growth Behavior of an Extra-Low-interstitial Titanium Alloy

Fatigue crack growth under mixed mode I-II loading with a single tensile overload at negative load ratios

Effect of single tensile overload on fatigue crack growth behavior of CP-Ti at negative load ratio

Fatigue Crack Growth Behavior of CP-Ti Cruciform Specimens with Mixed Mode I-II Crack under Biaxial Loading

Numerical Fatigue Crack Growth on Compact Tension Specimens under Mode I and Mixed-Mode (I+II) Loading

A Study on Fatigue Crack Closure Associated with the Growth of Long Crack in a New Titanium Alloy

Molecular dynamics simulation of effects of loading parameters on fatigue crack growth behavior in titanium single crystal

Study on mixed-mode fracture behavior of TC4 titanium alloy

THE MIXED-MODE PROPAGATION OF FATIGUE CRACK IN CTS SPECIMEN

A Study of Loading Path Influence on Fatigue Crack Growth under Combined Loading

Fatigue Crack Growth Behavior of Beta-Annealed Ti–6Al–2Sn–4Zr–xMo (x = 2, 4 and 6) Alloys: Influence of Microstructure and Stress Ratio

Effect of loading conditions on short fatigue crack propagation behaviours in cast Al Si alloys

Fatigue Crack Growth for Ferritic Steel under Negative Stress Ratio

Crack Initiation Mechanisms under Two Stress Ratios Up to Very-High-cycle Fatigue Regime for a Selective Laser Melted Ti-6Al-4V

Effect of Mode II in the mixed-mode on the fatigue crack growth behaviour for SAPH440 material

Fatigue cracking behavior and life assessment of TC11 titanium alloy in very high cycle regime at two working temperatures

Α-Lamella Orientation Dependence of Fatigue Crack Propagation in As-Forged TiB/near Α-Ti Composite

Influence of microstructure on fatigue crack growth behavior of Ti–6Al–3Nb–2Zr–1Mo alloy: Bimodal vs. lamellar structures