Influence of inversion defects and Cr–Cr pairs on the photoluminescent performance of ZnAl 2 O 4 crystals

Dong Zhang,Qingjie Guo,Yanfang Ren,Changzheng Wang,Qiang Shi,Qinglin Wang,Xia Xiao,Wenjun Wang,Quli Fan

DOI: https://doi.org/10.1007/s10971-017-4527-4

2017-01-01

Journal of Sol-Gel Science and Technology

Abstract:ZnAl 2 O 4 :Cr 3+ crystals were synthesized by using sol–gel method at 1000 °C. The results showed that with the concentration of Cr 3+ in spinel lattices increasing, the x-ray diffraction peaks shifted toward lower diffraction angles, and the grain size revealed a rapid increase and became invariable when the Cr 3+ dopant concentration was above 0.7 mol%. All the samples showed a series of emission peaks ranging from 660 to 730 nm assigned to spin-forbidden 2 E g → 4 A 2g transition of Cr 3+ ions in spinel lattices. The intensity of emission peaks revealed a strong dependence on the Cr 3+ concentration. An additional emission peak at 740 nm was present when the Cr 3+ ions concentration was above 0.5%. All emission peaks were quenched when the Cr 3+ concentration reaches 1.3 mol%. The results of x-ray photoelectron spectroscopy (XPS) and electron paramagnetic resonance (EPR) suggested that the Cr 3+ ions occupied the octahedral sites in spinel lattices, and with the Cr 3+ concentration increasing, the exchange interaction and coupling interaction between Cr–Cr were enhanced and the antisite defects related to Zn in octahedral sites increased. Graphical abstract