Abstract:The study particularly focuses on the effect of the Cr co-doping on the structural, optical and magnetic properties of Zn0.99Fe0.01O. Zn0.99-xFe0.01CrxO (x =0, 0.01, 0.03 and 0.05) nanoparticles. Powder x-ray diffraction (XRD) analysis confirms all the samples have hexagonal wurtzite structures. The average crystallite size (D) and microstrain of the samples were calculated using the Williamson-Hall relation and D was found to be 13 +- 1 nm for Zn0.99Fe0.01O. In Cr co-doped samples, D increase slightly with Cr content and are given by 9 +- 1, 10 +- 1, and 11 +- 1 nm for the samples with x = 0.01, 0.03 and 0.05, respectively; while the strain decreased with increase in Cr co-doping. Transmission electron microscopy (TEM) images of the samples indicate that particles are in the nano-regime and agglomerated. Particle sizes are found to be 14 +- 1, 11 +- 1 and 12 +- 1 nm for Zn0.99-xFe0.01CrxO with x = 0, 0.03 and 0.05, respectively. The substitution of Fe3+ and Cr3+ at Zn2+ sites has an impact on the optical properties. The band-gap decreases from 3.296 +- 0.002 eV to 3.258 +- 0.002 eV with increase of Cr concentration. Photoluminescence (PL) of Zn0.96Fe0.01Cr0.03O revealed the presence of defects, the emission peaks at 410 nm and 513 nm are attributed to Zn vacancies (VZn) and singly ionized oxygen vacancies, respectively. The M(-H) curves of Zn0.99-xFe0.01CrxO (x = 0.03 and 0.05) measured at room temperature using a vibrating sample magnetometer (VSM) are found to be hysteretic, signifying room temperature ferromagnetism (RTFM). Maximum saturation magnetization, 0.67 +- 0.01 emu.g-1, is observed in Zn0.94Fe0.01Cr0.05O. The observed RTFM in Fe+Cr co-doped ZnO is explained by of bound magnetic polaron (BMP) mechanism, the BMPs are formed by VZn and Vo^+ defects. This paper enhances the understanding of the origin of RTFM in Fe+Cr co-doped ZnO nanoparticles.

Effects of Cr-doping on the photoluminescence and ferromagnetism at room temperature in ZnO nanomaterials prepared by soft chemistry route

Effects of Cr-doping on the optical and magnetic properties in ZnO nanoparticles prepared by sol–gel method

Impact of Cr doping on the structure, optical and magnetic properties of nanocrystalline ZnO particles

Optical and ferromagnetic properties of Cr doped ZnO nanorods

Room-temperature Ferromagnetism in Lightly Cr-doped ZnO Nanoparticles

Effect of annealing temperature on structure, magnetic properties and optical characteristics in Zn0.97Cr0.03O nanoparticles

Intrinsic Ferromagnetic Properties in Cr-doped ZnO Diluted Magnetic Semiconductors

Effects of Cr Doping on Properties of La0.5Ca0.5MnxCr1−xO3 Films

Preparation of One-Dimensional Diluted Magnetic Semiconducting Cr0.046zn0.954o and Properties Tuning with H-2 Atmospheric Annealing

Oxygen Enhanced Ferromagnetism in Cr-doped ZnO Films

Structure, optical, and room-temperature ferromagnetic properties of pure and transition-metal-(Cr, Mn, and Ni)-doped ZnO nanocrystalline films grown by the sol-gel method

Room Temperature Ferromagnetic and Optical Properties of Chrome Doped ZnS Nanorods Prepared by Hydrothermal Method

Ferromagnetic properties in undoped and Cr-doped SnO2 nanowires

Effect of Cr, N co-doping on the structural and optical properties of ZnO thin films deposited by pulsed laser deposition

Structure, optical and magnetic properties of Fe doped, Fe+Cr co-doped ZnO nanoparticles

Tunable Ferromagnetic Behavior in Cr Doped Zno Nanorod Arrays Through Defect Engineering

Oxygen vacancies induced ferromagnetism in undoped and Cr doped SnO 2 nanowires

Structure and magnetic properties of Cr-doped ZnO nanoparticles prepared under high magnetic field

Synthesis and photoluminescence of Cr-doped rod-like ZnO particles by hydrothermal method

Magnetic Properties of Chromium-Doped Zno

A study of structural, optical and magnetic properties of Cr, Ce co-doping in ZnO diluted magnetic semiconductors