DOI: https://doi.org/10.1016/j.matchemphys.2020.123323
IF: 4.778
2020-10-01
Materials Chemistry and Physics
Abstract:The Pechini-type hydrothermal process was used to prepare Y3+ doped MgAl2O4: Cr3+ nanopowders. The effect of Y3+ on the structure, crystal field, and photoluminescence of MgAl2O4: Cr3+ was considered. The single phase of MgAl2O4 was obtained at the calcination temperature of 900–1200 °C. As the calcination temperature reached 1300 °C, the impurity phases Y3Al5O12 appeared, along with a trace of MgO. When Y3+ content was more than 3 mol%, Y3Al5O12 and MgO phase also existed. The Y3+ ions doped MgAl2O4: Cr3+ enhanced the photoluminescence of samples, and the emission of sample Y3 was 80% higher than that of Y0. Meanwhile, the Y3+ ions affected the position of absorption and excitation spectra and caused the change of crystal field surrounding Cr3+. The strongest absorption and excited bands shifted to longer wavelengths, and the 4A2-4A1 absorption of Cr3+ was enhanced. The Dq/B value of sample Y0 was 3.33, and it increased slightly as Y3+ doped. The Dq/B value of sample Y3 was 3.46. As an excellent sintering aid for the sintering process of MgAl2O4 transparent ceramics, Y2O3 is also helpful to enhance the photoluminescence of MgAl2O4: Cr3+.
materials science, multidisciplinary
What problem does this paper attempt to address?
This paper aims to explore the influence of Y3+ ions on the photoluminescence properties of MgAl2O4:Cr3+ nano - powders. Specifically, the researchers prepared MgAl2O4:Cr3+ nano - powders doped with different concentrations of Y3+ by the Pechini - type hydrothermal method, and analyzed the influence of Y3+ doping on the material structure, crystal field and photoluminescence characteristics. The study found that as the Y3+ content increases, the photoluminescence intensity of the sample is significantly enhanced. In particular, when the Y3+ doping amount is 3 mol%, its luminescence intensity is 80% higher than that of the sample without Y3+ doping. In addition, the introduction of Y3+ also leads to changes in the positions of absorption and excitation spectra, enhancing the energy transfer efficiency from the matrix to Cr3+, thereby improving the photoluminescence properties of the material. These results indicate that Y2O3 is not only an excellent additive in the sintering process of MgAl2O4 transparent ceramics, but also can effectively improve the luminescence performance of MgAl2O4:Cr3+.