Coherent effect of Er3+–Yb3+ co-doping on enhanced photoluminescence properties of Al2O3 powders by the sol–gel method

X.J Wang,M.K Lei,T Yang,B.S Cao

DOI: https://doi.org/10.1016/j.optmat.2004.01.011

IF: 3.754

2004-01-01

Optical Materials

Abstract:The Er3+–Yb3+ co-doped Al2O3 powders have been prepared by the sol–gel method, using the aluminium isopropoxide [Al(OC3H7)3]-derived Al2O3 sols with the addition of erbium nitrate [Er(NO3)3·5H2O] and ytterbium nitrate [Yb(NO3)3·5H2O]. The phase structure, including only two crystalline types of Al2O3 phases, γ and θ, was obtained for the 0–1 mol% Er3+ and 0–2 mol% Yb3+ co-doped Al2O3 powders at the different sintering temperature of 800–1000 °C. The evidence for indirect pumping of Er3+ through transfer of energy from Yb3+ was found in the Al2O3 matrix material. For the 0.5 mol% Er3+ and 0.5 mol% Yb3+, the 1.0 mol% Er3+ and 1.0 mol% Yb3+ co-doped Al2O3 powders, the photoluminescence (PL) peak intensity at 1.533 μm in the spectra increased by a factor of about 2, and the corresponding full widths at half maximum (FWHM) was increased to about 59 nm, compared with that of the 0.5 and 1 mol% Er3+-doped Al2O3 powders, respectively. At the same Er3+–Yb3+ co-doping concentration, the PL intensity increased with increasing the sintering temperature from 800 to 1000 °C. Coherent effect of Er3+–Yb3+ co-doping on enhanced PL properties of Al2O3 powders was observed. A proper molar ratio of 1:1 for Yb3+ and Er3+ led to the maximum PL intensity at the same sintering temperature.