Cr 3+ ions improving the spectral properties of YAG: Ce 3+ luminescent ceramics for white LD lighting
Xin Li,Chi Zhang,Jing Chen,Quansheng Liu,Zhaohui Bai,Xiuling Liu,Xiaoyun Mi
DOI: https://doi.org/10.1016/j.ceramint.2022.10.072
IF: 5.532
2022-12-22
Ceramics International
Abstract:The lack of red light emission in Y 3 Al 5 O 12 :Ce 3+ (YAG:Ce 3+ ) luminescent ceramics has resulted in high color temperature and low color rendering index for solid state illumination, such as, LED or LD. Therefore, Y 2.94 Al 5-x Cr x O 12 :0.06Ce 3+ (x = 0.004, 0.029, 0.054, 0.079, 0.104 mol) luminescent ceramics were prepared by vacuum sintering method. The doping of Cr 3+ ions caused the weak red emission peaks between 675 nm and 720 nm, and the luminescence intensity of red light increased first and then decreased with the increase of Cr 3+ ions doping content. The best doping concentration of Cr 3+ ions is 0.054 mol. And in the co-doped system of ceramics, we confirmed the energy transfer from Ce 3+ to Cr 3+ . YAG:Ce 3+ , Cr 3+ series ceramics yielded a slight shift in color coordinates towards the red light area. Meanwhile, as the concentration of Cr 3+ ions increasing, the color rendering index began to show an increasing trend with a maximum value of 79.4. The consequences display that Ce, Cr co-doped garnet luminescent ceramics are promising for red light supplementation and high CRI lighting applications of white LD.
materials science, ceramics